Superabsorbent Cellulose-Based Hydrogels Cross-linked with Borax PDF

www.nature.com/scientificreports OPEN Superabsorbent cellulose‑based hydrogels cross‑liked with borax Supachok Tanpichai1,2, Farin Phoothong3 & Anyaporn Boonmahitthisud4,5,6*...

www.nature.com/scientificreports OPEN Superabsorbent cellulose‑based hydrogels cross‑liked with borax Supachok Tanpichai1,2, Farin Phoothong3 & Anyaporn Boonmahitthisud4,5,6* Cellulose, the most abundant biopolymer on Earth, has been widely attracted owing to availability, intoxicity, and biodegradability. Environmentally friendly hydrogels were successfully prepared from water hyacinth-extracted cellulose using a dissolution approach with sodium hydroxide and urea, and sodium tetraborate decahydrate (borax) was used to generate cross-linking between hydroxyl groups of cellulose chains. The incorporation of borax could provide the superabsorbent feature into the cellulose hydrogels. The uncross-linked cellulose hydrogels had a swelling ratio of 325%, while the swelling ratio of the cross-linked hydrogels could achieve ~ 900%. With increasing borax concentrations, gel fraction of the cross-linked hydrogels increased considerably. Borax also formed char on cellulose surfaces and generated water with direct contact with flame, resulting in flame ignition and propagation delay. Moreover, the cross-linked cellulose-based hydrogels showed antibacterial activity for gram-positive bacteria (S. aureus). The superabsorbent cross-linked cellulose- based hydrogels prepared in this work could possibly be used for wound dressing, agricultural, and flame retardant coating applications. Hydrogels, three-dimensional porous cross-linked network of macromolecular materials made from hydrophilic polymers with ability to absorb and retain significant quantities of water and resistance to dissolution, have been widely used in many fields such as food, medical, pharmaceutical, agricultural, cosmetic, sensor, and waste treatment. Bio-based hydrogels derived from natural resources including cellulose, hyaluronate, alginate, starch, gelatin, chitin, and chitosan have recently received much attention due to their biodegradability, biocompat- ibility, and environmental ­sustainability1–3. Among these natural resources, cellulose exhibits a very high yield and mainly derived from plants which are abundant and can be replenished ­naturally4,5. Water hyacinth (Eichhornia crasspies) is an aquatic weed which causes a negative impact on the environment due to their extremely fast growth rate, the impediment to water flow, an enormous water loss through evapo- transpiration, and the blocking waterways, disturbing underwater life such as fish and other p ­ lants6–8. Due to its porous structure and low lignin content (~ 5–9 wt%) compared with other plants, water hyacinth would be an alternative material for cellulose ­extraction7,8. Prior to forming a hydrogel, cellulose is required to dissolve in a specific solvent or condition to form a liquid solution because cellulose consists of abundant reactive hydroxyl groups (-OH groups) on its structure, leading to the strong intra- and inter-molecular hydrogen bonds forming highly crystalline domains. In this study, the mixture of NaOH/urea solution was selected to dissolve the extracted cellulose from water hyacinth at low temperature due to its low toxicity, quick dissolution time, and low ­cost5,9. The abundant reactive hydroxyl groups (–OH groups) on cellulose molecules lead to high water absorbency and generation of the cross-linked structure. The cross-linking in hydrogels can be generated by three main methods: physical, chemical, and radia- tion methods. The advantages and drawbacks of each method are listed in Table 110–14. Due to the stability and high strength, the chemical cross-linking method was chosen to prepare cellulose hydrogels in this study. However, the main disadvantage of this method is the toxicity of residual cross-linking agents. Therefore, there are many efforts to use low toxic crosslinkers such as c­ arbodiimide15, ­borax12,16,17, sodium ­trimetaphosphate18,19, N,N′-methylene ­bisacrylamide20, and polycarboxylic a­ cids21–23. Borax (sodium tetraborate, N ­ a2B4O7.10H2O), known as a non-toxic food additive, is an interesting candidate as a chemical cross-linker due to its low toxicity, low cost, and water-soluble a­ bility12,16,17,24. Borax in an aque- ous solution can be dissociated into trigonal boric acid (B(OH)3) and tetrahydroxy borate ion (B(OH)4–) which 1 Learning Institute, King Mongkut’s University of Technology Thonburi, Bangkok 10140, Thailand. 2Cellulose and Bio‑Based Nanomaterials Research Group, King Mongkut’s University of Technology Thonburi, Bangkok 10140, Thailand. 3Program of Petrochemical and Polymer Science, Faculty of Science, Chulalongkorn University, Bangkok 10330, Thailand. 4Department of Materials Science, Faculty of Science, Chulalongkorn University, Bangkok 10330, Thailand. 5Green Materials for Industrial Application Research Unit, Faculty of Science, Chulalongkorn University, Bangkok 10330, Thailand. 6Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University, Bangkok 10330, Thailand. *email: [email protected] Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 1 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ Methods Advantages Drawbacks - Poor stability of hydrogels - No use of chemical crosslinking agents - Weak cross-linking bonding Physical cross-linking - Reversible cross-linking - Difficulty to control the cross-linking density - Poor mechanical strength - Stable hydrogels - Strong cross-linked bonding Chemical cross-linking - Toxicity of residual cross-linking agents - High cross-linking density - High mechanical strength - No requirement for catalysts or additives to initiate a reac- - Weak mechanical strength Radiation cross-linking tion - High cost and energy consumption - Possibility to control cross-linking points Table 1.  Advantages and drawbacks of cross-linking methods to form hydrogels 10–14. Figure 1.  Cross-linking mechanisms between hydroxyl groups of polymers and borax as a cross-linker. are able to react with functional groups of polymers, and then the didiol cross-linking by either covalent or hydrogen bonding is f­ ormed12,17,25–27, as shown in Fig. 1. The cross-linking of didiol-borax complexes generated by tetrahydroborate ions from borax has been found to be dominated by the p ­ H28–30. Increasing the pH of the system, larger amounts of tetrahydroborate ions were generated, and the higher cross-linking reaction could be made from these i­ons28. This resulted in higher mechanical properties (tensile stress and Young’s modulus) of the cross-linked poly(vinyl acetate) films when the films were prepared at a pH of 11 in comparison to those of the cross-linked films prepared at a pH of 4 owing to a higher degree of cross-linking28. Although borax has been successfully used to form cross-linking in various hydrogels such as ­starch25, poly(vinyl alcohol)12,17, and guar g­ um26, studies of the use of borax in cellulose hydrogels have been limited. Here, we prepared cross-linked cellulose hydrogels by a dissolution approach using a mixed NaOH/urea solvent (a pH of 11) with aids of borax, and effects of borax concentrations on chemical structure change, crystallinity, thermal stability, morphology, swelling ratio, gel fraction, and antibacterial ability of the cellulose hydrogels were investigated. The utilization of borax as a cross-linking agent would be an environmentally friendly approach to yield the cross-linked cellulose-based hydrogels with high water absorption. Experimental Materials. Water hyacinth fibers (Eichornia crassipes) were obtained from the water hyacinth community enterprise (Baan Pak Tob Chawa) in Phra Nakhon Si Ayutthaya province, Thailand. Ethanol and toluene (Com- mercial grade, 95% purity) were purchased from CT Chemical Co., Ltd. Analytical-grade Hydrochloric acid (HCl, Conc. 37%) was purchased from JT Baker Chemicals Company, while sodium hydroxide (NaOH, 98% purity) and sodium hypochlorite (NaClO, 4–6% available chlorine) were supplied from Loba Chemie Pvt. Ltd. Urea and borax (> 99% purity) were purchased from Ajax Finechem Pvt. Ltd. and Quality Reagent Chemical Company, respectively. All chemicals and reagents were used as received without further purification. Purification of water hyacinth fibers. Water hyacinth fibers were dewaxed with 500 ml mixture solution of toluene-ethanol at 2/1 volume ratio at 75 °C for 3 h. The fibers were subsequently washed and dried at 60 °C for 24 h. The dewaxed water hyacinth fibers were treated by alkaline treatment, bleaching, and acid hydrolysis. 10 g of the fibers was bleached using 3 v/v% NaClO at 80 °C for 2 h, and the bleached fibers were later subjected to alkaline treatment using 1 w/v% NaOH at 60 °C for 2 h to remove hemicellulose. After that, the bleaching process was repeated to obtain purified cellulose, and the purified cellulose was acid-treated using 5 v/v% HCl at 60 °C for 6 h. The treated fibers were washed with distilled water to remove the chemical excess. The treated- cellulose fibers coded as “F” were further used for characterizations and preparation of the cellulose solutions. Preparation of cross‑liked cellulose‑based hydrogels with borax. The cross-linked cellulose-based hydrogels with borax were prepared by dissolving 3 g of dried chemical-treated cellulose fibers into an aqueous Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 2 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) www.nature.com/scientificreports/ solution of 7% NaOH and 12% urea at a low temperature of ~ − 12 °C with vigorous stirring for 3 min to obtain a transparent cellulose s­ olution31. After that, the prepared cellulose solution was mixed with various concentra- tions of borax at room temperature with continuous stirring for 5 min. The weight ratios of cellulose and borax were: 1:0, 1:1, 1:2, 1:3, 1:4 and 1:5. These samples were coded as B0, B1, B2, B3, B4 and B5, respectively. After that, 30 mL of the cellulose-borax solution was poured into a 9 cm-diameter Petri dish and kept at room temperature for 3 days to yield a hydrogel. All hydrogel samples were washed in excess deionized water (DI water) to remove the unreacted components and kept in a plastic container filled with DI water for further characterization. Characterization. Fourier‑transform infrared spectroscopy. Functional group analysis of the water hya- cinth fibers, treated cellulose fibers, and cross-linked cellulose-based hydrogels was carried out using a Fourier- transform infrared spectroscope (FTIR) (Nicolet 6700, Thermo Fisher Scientific Co., Lid, USA) in the range from 4,000 to 400 ­cm-1. The dried samples were ground with KBr, and the mixture was pressed into a clear disk for spectrum recording. X‑ray diffraction. The crystallinity pattern of the water hyacinth fibers, treated cellulose fibers, and cross-linked cellulose-based hydrogels was determined by x-ray diffraction (XRD) (D8 Advance, Bruker Corp., USA) oper- ated at 40 kV and 40 mA. The samples were scanned over a range of 5 to 60° at 2θ with the count step size of 0.5 s and a step size of 0.02°. The crystallinity index was determined with Segal’s empirical m­ ethod32 as followed: Crystallinity index (%) = ((I200 −Iam )/I200 ) × 100 (1) where I200 is the maximum intensity of the principal peak of 200 located at 2θ = 22°, which represents the crystal part, and the minimum intensity of the peak located at 2θ = 16.5° and 22.6°, corresponding to the amorphous part. Thermalgravimetric analysis. The thermal stability of the water hyacinth fibers, treated cellulose fibers, and cross-linked cellulose-based hydrogels was evaluated by thermogravimetric analysis (TGA) (TGA/SDTA 8­ 51e, Mettler Toledo LLC, USA) under a nitrogen atmosphere with a flow rate of 40 ml ­min-1 at a heating rate of 10 °C ­min-1 over the temperature range of 50–700 °C to investigate the thermal degradation and residue of the samples. UV–vis spectroscopy. The optical transmittance of the cross-linked cellulose-based hydrogels was measured at wavelength from 400 to 700 nm using a UV–Vis spectrophotometer (CE7000, X-Rite, USA). The data were col- lected at a scan speed of 240 nm ­min-1. Scanning electron microscopy. The cross-section morphological characterization of the cross-linked cellulose- based hydrogels was examined by scanning electron microscope (SEM) (JSM-6610LV, JEOL Ltd., Japan) at an accelerated voltage of 10 kV. The hydrogel samples after swelling in DI water (to an equilibrium swelling) were fractured after lyophilization using a freeze drier (BETA 1–8 LD plus, Martin Christ Gefriertrocknungsanlagen, Germany). Prior to each measurement, the fractured surface of the dried hydrogel sample was sputter coated with a thin layer of gold to prevent charging during the SEM operation. Water content, swelling ratio and gel fraction measurement. The cross-linked cellulose-based hydrogels were immersed in DI water for 24 h to achieve equilibrium swelling. After removal of immoderate surface water, a fully swollen hydrogel was weighted (ws). Then, the swollen hydrogels were freeze-dried and weighted (wd) to calculate the water content and swelling ratio according to the following equations: water content (%) = ((ws −wd )/ws ) × 100 (2) swelling ratio (%) = ((ws −wd )/wd ) × 100 (3) The gel fraction of the samples was calculated using the following equation. gel fraction (%) = (wfinal /winitial ) × 100 (4) where winitial is the weight of the freeze-dried hydrogel, and wfinal is the weight of the dried undissolving part obtained by dissolving the freeze-dried hydrogel into the aqueous solvent of 7% NaOH/12% urea at a tempera- ture of − 12 °C. Antibacterial activity test. The antibacterial activity test of the selected cellulose-based hydrogel was evaluated using the AATCC 100 standard. Prior to characterization, the dried cellulose-based hydrogel film was prepared into 5 × 5 cm. E. coli (gram-negative bacteria) and S. aureus (gram-positive bacteria) were used as a testing strain to evaluate the antibacterial activity of the hydrogel films. The surface of the films was applied with 1­ 06 CFU/ml of those bacterial strains. After that, the prepared films were incubated at 37 °C for 24 h and washed with the fresh broth. The broth that recovered from the specimen was dispersed onto the agar plate an incubated at 37 °C for 24 h. The antibacterial effectiveness of the samples was determined by the percentage reduction of bacteria calculated by the following equation. % Reduction of bacteria = ((B − A)/B) × 100 (5) Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 3 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ Figure 2.  Fourier-transform infrared (FTIR) spectra of purified water hyacinth fibers (F) and cross-linked hydrogels with various concentrations of borax in the range of (a) 4,000 – 400 c­ m-1 and (b) 1,500 – 1,100 ­cm-1. where A and B are the number of bacteria colonies before and after incubation for 24 h, respectively. Results and discussion Chemical changes. Effects of dissolution with a mixed NaOH/urea solvent and different loadings of borax on changes in the chemical and crystallographic structure of cellulose were differentiated by FTIR. FTIR spectra of water hyacinth fibers and cross-linked cellulose hydrogels with different borax concentrations are presented in Fig. 2. Purified cellulose fibers have distinguished peaks initially located at 3,330 and 3,290 ­cm-1, corresponding to OH regions generated by O(3)H–O(5) intramolecular hydrogen b ­ onding33–36. The typical peaks of cellulose I located at 1,430 ­cm-1 (symmetric C ­ H2 bending vibrations), 1,374 ­cm-1 (C–H deformation), 1,316 ­cm-1 ­(CH2 wagging), 1,160 ­cm-1 (symmetric ring stretching), 1,060 ­cm-1 (C–O stretching vibration), and 895 ­cm-1 (asym- metric out-of-plane ring stretching) were observed from these purified cellulose ­fibers35–37. After dissolution in mixed NaOH/urea solvent, the differentiation of these typical peaks was observed in comparison to those of the purified cellulose. It was found that the regenerated cellulose hydrogels presented the cellulose II characteristic with the disappearance or lower intensity of the typical peaks of cellulose ­I38. The flattening of the 3,330 and 3,290 ­cm−1 peak occurred, and two new local maxima appeared at 3,440 and 3,490 ­cm−1. This was associated with an occurrence of a shoulder at 3,130 ­cm−1. The peak located at 1,430 ­cm−1, assigned to ­CH2 stretching of cellu- lose, shifted to 1,420 ­cm−1 due to changes of the hydroxymethyl group at the C(6) ­position33,38,39, while the band at 1,110 ­cm−1 ­disappeared38. This was an indication of the complete transformation from cellulose I to cellulose II caused by the formation of new intermolecular and intramolecular hydrogen bonding. With the introduction of borax, there were characteristic peaks of borax and borate occurring in the FTIR spectra at 1,330 and 1,278 ­cm−1, assigned to asymmetric stretching relaxation of B–O–C16,40,41. The appearance of these peaks could confirm the formation of the covalent cross-linking network between borate ions and hydroxyl groups of c­ ellulose27,42. Also additionally, the hydrogen-bonded crosslinking could be formed between the ring structures of cellulose chain and ­borax27. During the hydrogel preparation, the pH of the cellulose solution prepared with a mixed NaOH/urea solvent was ⁓11, larger amounts of tetrahydroborate ions generated from borax played a vital role in the cross-linking formation. Although the combined cross-linking mechanisms were formed in the system, it would be difficult to measure which cross-linking structure mainly o ­ ccur27,42. Similar formation of complexes between hydroxyl functional groups of poly(vinyl alcohol) and cellulose with aids of borax as a cross-linking agent has been r­ eported40,43–45. Crystallinity. Changes of crystallinity and crystalline forms after dissolution and cross-linking could be dif- ferentiated from XRD patterns. Figure 3 presents XRD patterns of the purified fibers and cross-linked cellulose hydrogels with different concentrations of borax. As expected, the cellulose I structure with the peaks located at 14.8, 16.5 and 22.6° lattice planes, corresponding to (1 − 1 0), (1 1 0) and (0 0 2) was observed for the puri- fied water hyacinth ­fibers34,39. This cellulose I structure can be generally found in natural fibers such as ­cotton39, pineapple ­leaves46,47, wood p ­ ulp48,49, ­eucalyptus37, and a­ baca37. After the water hyacinth fibers were dissolved in a mixed solution of NaOH and urea, the XRD patterns of the regenerated cellulose were transformed from the cellulose I to cellulose II structure with peaks located at 12.0, 20.2 and 22.5°, attributed to (1 − 1 0), (1 1 0) and (0 0 2) lattice planes, respectively. Wei et al.34 found that dissolution temperatures of the mixed NaOH/ urea solution affected an amount of cellulose I and II in cellulose materials. The mixed solution with a lower temperature could convert a higher amount of cellulose I to cellulose II. The complete disappearance of the peaks related to a cellulose I structure was found when the cellulose was dissolved at temperature of − 12.5 °C, Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 4 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) www.nature.com/scientificreports/ Figure 3.  X-ray diffraction (XRD) patterns of purified water hyacinth fibers (F) and cross-linked cellulose hydrogels with various concentrations of borax. indicating the complete dissolution of cellulose. In this work, the complete conversion of the cellulose structure from cellulose I to cellulose II was observed because the temperature during the dissolution was controlled to be ~ − 12.5 °C. Moreover, the dissolution treatment time is another factor to dominate the conversion of the cel- lulose ­structure48. The crystallinity index of the water hyacinth fibers was 77.1%, and this crystallinity degree was reduced to 71.1% after regeneration with the mixed solvent of NaOH and urea. This reduced crystalline regions could be owing to the combined mechanisms: the disruption of original inter- and intra-molecular interaction of cellulose molecules by NaOH, the reduction of cellulose aggregates in the cellulose-NaOH complex by urea hydrates, and rearrangement of new hydrogen bond between hydroxyl groups of cellulose in the cellulose-NaOH ­complex35,39,50. A similar reduction in the crystallinity index of regenerated cellulose was reported in comparison with that of original ­fibers34,35. When various loadings of borax were introduced into the regenerated cellulose hydrogels, no change in the cellulose structure was observed. However, a concentration of borax could increase the percentage of the crys- talline regions of the cross-linked regenerated cellulose materials. The uncross-linked hydrogel samples (B0) had a crystallinity index of 70.25%, and with the addition of borax, the crystallinity of the B1 and B3 samples increased to 71.76 and 76.51%, respectively. This increase in crystallinity might be attributed to an increase of bonding between cellulose. However, the crystallinity of the cross-linked B5 hydrogels decreased. The similar reduction in crystallinity was found by Zhang et al.51. Borax could destroy intermolecular and intermolecular hydrogen bonding of cellulose in the crystalline area, and B–O–C bonding would be formed between cellulose molecules, and this would restrict the mobility of cellulose c­ hains41. Moreover, it was reported that borax could partly change the cellulose structure form cellulose I to cellulose ­II51. Thermal properties. Effects of dissolution and cross-linking on thermal stability of cellulose hydrogels were investigated by thermogravimetric analysis (TGA), and the TGA and derivative thermogravimetric (DTG) curves of these cellulose samples are presented in Fig. 4. The initial thermal decomposition state at temperature of less than 100 °C is caused by the moisture evaporation from cellulose m ­ aterials52. The second thermal degra- dation stage occurs between 250 and 400 °C, corresponding to the thermal degradation of ­cellulose53. It should be noted that there are no thermal transition stages of hemicellulose and lignin found in the curves due to the removal of hemicellulose and lignin by the chemical treatments during the fiber purification step. This resulted in a single peak occurring in a DTG curve. A change in thermal stability of the cellulose materials was noticeable after the dissolution of cellulose fibers. The lower thermal degradation of the B0 materials was observed due to the decomposition of the re-formed crystalline regions (Cellulose II) by the NaOH/urea s­ olvent34,54. Moreover, the char content at 700 °C found in the B0 samples was 20.57%, which was significantly higher than that of the cellulose fibers (9.13%). This higher amount of remnants generated from the B0 materials was due to the fact that cellulose II would generate larger amounts of graphite carbon than cellulose I­ 34. Additionally, the dissolu- tion temperature affected thermal stability and char formation of the dissolved c­ ellulose34. Cellulose dissolved at temperature of − 12.5 °C exhibited lower thermal stability and a larger content of char residues in comparison to those of cellulose materials prepared at the temperature range of 2–10 °C34. With the addition of borax, there are three thermal decomposition states happening. The first thermal decom- position state occurs between 50 and 200 °C owing to the moisture evaporation from borax, and the second transition state is the cellulose degradation which begins between 250 and 350 °C55–57. The formation of com- plexes between cellulose and boron is the final thermal step between 360 and 410 °C55. It was found that the onset temperature of cross-linked cellulose hydrogels decreased in comparison to those of uncross-linked hydrogels Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 5 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ Figure 4.  (a) Thermogravimetric (TG) and (b) derivative thermogravimetric (DTG) curves of purified water hyacinth fibers and cross-linked hydrogels with various concentrations of borax. Figure 5.  Transmittance of the cross-linked cellulose hydrogels with borax. (B0). This could be attributed to the dehydration of moisture from borax. With increasing borax loadings, a per- centage of the weight loss at this stage became g­ reater54,55. Borax would play a key role to cause the early thermal ­degradation55,56. Moreover, the maximum thermal decomposition temperature (Tmax) of the cross-linked cellulose hydrogels decreased when a larger amount of borax was applied into the hydrogels. Tmax of the B0 material was 339.9 °C, while the addition of borax decreased Tmax of the B1 sample to 330.5 °C. With increasing the borax concentrations, Tmax of the cross-linked cellulose materials was shifted towards a lower temperature. The B5 hydrogels had Tmax of 309.3 °C. This decrease in thermal stabilities of the cross-linked cellulose hydrogels with a higher amount of borax could be due to the esterification of cellulose with ­borax55. A decrease in the DTG peak height was observed when borax was introduced, and the cross-linked cellulose hydrogels with higher contents of borax presented the lower peak height. This reduction could be attributed to thermal annealing of borax and cellulose, which resulted in a slower degradation r­ ate55. The total char formed at 700 °C was found to be dependent on the borax concentration. With the incorpora- tion of borax, the total residue increased from 20.57 (B0) to 23.46% (B1). With a higher content of borax loaded into the cellulose hydrogels, a greater content of the residue was found. The total residue of the B5 sample was 28.45%. The combination of the char formation on cellulose surfaces and generation of water from borax residue and hydroxyl groups of cellulose is an insulator to delay flame ignition and p ­ ropagation56,58,59. This was well- agreed with the fire testing results. The dried B0 sample had a fire growth rate of 1.43 mm ­s-1, while the fire growth rate plummeted to 0.63 mm ­s-1 for the B1 material. This fire growth rate considerably decreased with increasing borax concentrations. The fire growth rate of 0.25 mm ­s-1 was measured from the B5 sample. Transparency. Figure 5 presents transparency of the cross-linked cellulose hydrogels with different loadings of borax investigated by UV–vis spectroscopy. 68.8% of the light could pass through the uncross-linked hydro- Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 6 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) www.nature.com/scientificreports/ Figure 6.  Scanning election microscopy (SEM) images of the cross-linked hydrogels with various concentrations of borax after freeze-drying. gels (B0) at 600 nm, and with the introduction borax the B1 sample presented a similar transparency to that of B0. However, the transparency of the cross-linked B4 and B5 hydrogels decreased. The transparency of the B5 materials reduced to 49.4% at 600 nm. This might be because more tetrahydroborate ions could from cross- linking in the hydrogels, which blocks or scatters the light. A similar decrease in transparency was reported with the addition of boric acid (BA) into poly(vinyl alcohol) ­films41. Morphology. The morphologies of cross-linked cellulose hydrogels with various contents of borax are pre- sented in Fig. 6. The uncross-linked cellulose hydrogel showed a compact structure. This would be due to the interconnection of cellulose chains via hydrogen bonding. A similar compact structure was reported for a car- boxymethyl cellulose-chitosan composite hydrogel without any introduction of cross-linkers60. On the other hand, with the introduction of borax the porous structure was observed. The B1 hydrogel presented intercon- nected network with pore diameters of less than 50 µm. This porous structure might be formed by the dense network of cellulose chains with borax. This similar porous structure was also reported for the hydrogels with the addition of citric acid and tartaric ­acid60. The interconnected porous structure was more prominent when the borax concentration was higher. The formation of cross-linking between hydroxyl groups in cellulose chains induced by borax could generate interconnected pore within the dense network structure of cellulose (B3 and B5). This interconnected porous structure induced by borax would affect mechanical properties of the cross- linked cellulose hydrogels. This would be our future work to study mechanical performances of the cross-linked cellulose hydrogels with borax. Figure 7 presents cross-linking reaction between cellulose chains which could generate voids within hydrogels at high loadings of borax. Water content, swelling ratio, and gel fraction. The water content in the cellulose hydrogels with borax is presented in Table 2. The uncross-linked cellulose hydrogels (B0) contained water of 90.8%, while with the incorporation of borax, the water content contained in the cross-linked B1 hydrogels increased to 92.6%. When the borax loading was higher, a higher content of water in the cross-linked hydrogels could be obtained. A value of 93.0% for the water content of the B5 hydrogels was reported. This might be because of higher amounts of functional hydroxyl groups generated from borax and cellulose reaction such as monodiol-borax complex interacted with water. It should be noted that the solid content plays a key role to dominate the water content of ­hydrogels61. A hydrogel with a higher solid content would contain less water, compared to a hydrogel with a lower solid content. The water content in the as-prepared hydrogels in this work was similar to that of the hydro- gels prepared from poly(vinyl alcohol)61. Swelling ratio is the capacity of the dried material to absorb water, which is one of the most important param- eters for hydrogel a­ pplications62. Table 2 presents the swelling ratio of the cross-linked cellulose hydrogels with borax. The uncross-linked cellulose hydrogels (B0) presented the swelling ratio of 325.2%, which was higher than that of poly(vinyl alcohol) hydrogels prepared using a freeze–thaw ­approach63. This higher swelling ratio was attributed to hydroxyl groups on cellulose surfaces which attracted water into the ­hydrogels62. The swelling ratio significantly increased to 553.1% with the introduction of borax. Then, a considerable increase in the swell- ing ratio was observed for B3 (the swelling ratio of 877%). This increase would be attributed to larger amounts Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 7 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ Figure 7.  Schematic illustration of cross-linking reaction between cellulose chains at a low and high concentration of borax. Materials Water content (%) Swelling ratio (%) Gel fraction (%) B0 90.8 ± 0.4a 325.2 ± 33.6a 2.2 ± 0.3a B1 92.6 ± 0.1b 553.1 ± 13.4b 8.8 ± 0.2b c c B2 92.8 ± 0.1 772.4 ± 13.5 10.3 ± 1.5b d d B3 93.5 ± 0.1 877.3 ± 44.4 17.3 ± 3.1c e d B4 93.2 ± 0.1 828.2 ± 9.9 18.0 ± 2.6c f d B5 93.0 ± 0.2 831.0 ± 50.1 21.3 ± 0.5d Table 2.  Water content, swelling ratio, and gel fraction of the cellulose hydrogels with different loadings of borax. Different letters indicate significant difference (p < 0.05) among samples measured under the same testing condition. Significant values are in [a, b, c, d, e, f]. of hydroxyl groups on cellulose molecules generated by borax to form hydrogen bonding with water associated with the porous ­structure64. An increment of the swelling capacity of poly(acrylamide-co-acrylic acid) hydrogels was found with the introduction of spirulina owing to the formation of hydrogen bonding between functional groups on the spirulina surface including hydroxyl, amide, and carboxyl g­ roups64. However, no change of the swelling ratio could be observed for the B4 and B5 hydrogels. This might be owing to the limited content of cellulose which could be interacted with tetrahydroborate ions. It was worth noting that the swelling ratio of the prepared cross-linked hydrogels was higher than that of hydrogels previously ­reported60,65. When hydrogels are stimulated by temperature, pH, ionic strength, magnetic field, and radiation, the hydrogel materials would either swell or ­shrink66,67. For example, an increase or decrease in the electrostatic repulsion between polymer chains occurs with a change in environmental pH, resulting in a swell or shrink characteristic of ­hydrogels62. It was reported that the cellulose hydrogels followed the second-order swelling k­ inetics62,68,69. In the initial swell- ing stage, the hydrogen bonding formed between adjacent cellulose chains limited the swelling of the cellulose networks. While the hydrogen bonds were being broken by water, the expansion of cellulose network was found, and water was accommodated in the cellulose network by osmotic pressure. The swelling capacity of this system achieves the equilibrium a­ symptotically68,69. The gel fraction was investigated to confirm the cross-linking occurring between tetrahydroborate ions and hydroxyl groups of cellulose. After immersing in the mixed NaOH/urea solvent, only 2.2% of the dried material remained intact, indicating the hydrogen bonding between cellulose chains took place in this uncross-linked hydrogels. However, with the addition of borax, the gel fraction increased to 8.8% for B1. This could be attrib- uted to the occurrence of the cross-linking. With increasing the borax concentrations, a value of the gel fraction increased considerably. B5 presented the gel fraction of 21.3%. This increase resulted from large amounts of tet- rahydroborate ions interacted with hydroxyl groups of cellulose. The low value of the gel fraction obtained from the cross-linked cellulose hydrogels prepared in this work might be owing to the lower degree of polymerization Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 8 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) www.nature.com/scientificreports/ Materials % reduction of E.coli % reduction of S. aureus B3 − 5.11 20.7 Table 3.  The percent reduction of E. coli bacteria and S. aureus bacteria of the cellulose hydrogel with the weight ratios of cellulose and borax of 1 to 3. and molecular weight of cellulose which limited the mobility of the molecular chains. Moreover, Geng et al.28 reported that the gel fraction of the cross-linked poly(vinyl acetate) with borax was mainly controlled by the pH when a concentration of borax was more than a threshold. The gel fraction of cross-linked poly(vinyl acetate) hydrogels with borax prepared at the pH of 11 (~ 70%) was higher than that of the hydrogels prepared at the pH of 9.3 (~ 64%). Therefore, an increase in the pH during the gel preparation step might fabricate hydrogels with a higher degree of cross-linking. Antibacterial property. It is known that the cellulose-based hydrogel does not possess antibacterial activ- ity which is the limitation to use in medical applications. Therefore, there are many attempts to introduce parti- cles to improve the antibacterial activity, such as silver nanoparticles, and graphene ­oxide23,70. In this research, it was found that the addition of borax not only produced the cross-linked structure of the cellulose-based hydro- gel, but also enhanced its antibacterial activity as shown the percentage reduction of bacteria in Table 3. The B3 hydrogel was chosen for the antibacterial activity characterization. The result showed that the incorporation of borax into cellulose-based hydrogel showed negative results of % reduction of bacteria for gram-negative bacte- ria (E. Coli) testing; it could not destroy gram-negative bacteria. On the contrary, The B3 sample exhibited the antibacterial activity for gram-positive bacteria (S. aureus) with 20.7 percent reduction. This might be because the existence of borax was able to destroy the gram-positive bacteria as compared to that of the gram-negative ­bacteria71. Conclusion The cellulose solution was initially prepared from water hyacinth fibers with a mixed solvent of urea and NaOH. The transformation from cellulose I to cellulose II was noticed after cellulose dissolution with an aid of the mixed solvent of NaOH and urea. This resulted in a lower degree of crystallinity and weaker thermal stability. Cellulose hydrogels formed by this cellulose solution had a water content of 90.8% and swelling ratio of 325.2%, and gel fraction of this hydrogel is as low as 2.2%. After that, borax was used as a cross-linker to fabricate cross-linked cellulose hydrogels, the swelling ratio and gel fraction increased significantly. Due to cross-linking occurring between tetrahydroborate ions and hydroxyl groups of cellulose, the cross-linked hydrogels could absorb larger amounts of water (900% of the original weight). The architecture of the as-prepared cross-linked hydrogels became porous, while the morphology of the uncross-linked hydrogels was compact. With increasing the borax content, more cavities were connected. The cross-linked hydrogels presented poorer thermal stability with the lower degradation temperature in comparison to the uncross-linked hydrogels. This was due to the esterification of cellulose caused by borax. However, a higher char yield of the cross-linked materials was observed. Moreo- ver, the antibacterial activitiy exhibited the existence of borax effectively destroyed the gram-positive bacteria. Therefore, the prepared cross-linked hydrogels would be useful for superabsorbent wound dressing, agricultural, and flame retardant coating applications. Data availability The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request. Received: 28 January 2022; Accepted: 12 May 2022 References 1. Bauli, C. R., Lima, G. F., De Souza, A. G., Ferreira, R. R. & Rosa, D. S. Eco-friendly carboxymethyl cellulose hydrogels filled with nanocellulose or nanoclays for agriculture applications as soil conditioning and nutrient carrier and their impact on cucumber growing. Colloids Surf. A. Physicochem. Eng. Asp. 623, 126771. https://​doi.​org/​10.​1016/j.​colsu​rfa.​2021.​126771 (2021). 2. Pei, Z. et al. Self-healing and toughness cellulose nanocrystals nanocomposite hydrogels for strain-sensitive wearable flexible sensor. Int. J. Biol. Macromol. 179, 324–332. https://​doi.​org/​10.​1016/j.​ijbio​mac.​2021.​03.​023 (2021). 3. Boonmahitthisud, A., Nakajima, L., Nguyen, K. D. & Kobayashi, T. Composite effect of silica nanoparticle on the mechanical properties of cellulose-based hydrogels derived from cottonseed hulls. J. Appl. Polym. Sci. 134, 44557. https://​doi.​org/​10.​1002/​ app.​44557 (2017). 4. Tanpichai, S. Recent development of plant-derived nanocellulose in polymer nanocomposite foams and multifunctional applica- tions: a mini-review. Express Polym. Lett. 16, 52–74. https://​doi.​org/​10.​3144/​expre​sspol​ymlett.​2022.5 (2022). 5. Tanpichai, S., Boonmahitthisud, A., Soykeabkaew, N. & Ongthip, L. Review of the recent developments in all-cellulose nanocom- posites: properties and applications. Carbohydr. Polym. 286, 119192. https://​doi.​org/​10.​1016/j.​carbp​ol.​2022.​119192 (2022). 6. Pakutsah, K. & Aht-Ong, D. Facile isolation of cellulose nanofibers from water hyacinth using water-based mechanical defibril- lation: Insights into morphological, physical, and rheological properties. Int. J. Biol. Macromol. 145, 64–76. https://​doi.​org/​10.​ 1016/j.​ijbio​mac.​2019.​12.​172 (2020). 7. Tanpichai, S., Biswas, S. K., Witayakran, S. & Yano, H. Water Hyacinth: a sustainable lignin-poor cellulose source for the produc- tion of cellulose nanofibers. ACS Sustain. Chem. Eng. 7, 18884–18893. https://​doi.​org/​10.​1021/​acssu​schem​eng.​9b040​95 (2019). Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 9 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ 8. Tanpichai, S. et al. Extraction of nanofibrillated cellulose from water hyacinth using a high speed homogenizer. J. Nat. Fibers https://​ doi.​org/​10.​1080/​15440​478.​2021.​18894​32 (2021). 9. Li, M.-F., Sun, S.-N., Xu, F. & Sun, R.-C. Cold NaOH/urea aqueous dissolved cellulose for benzylation: synthesis and characteriza- tion. Eur. Polym. J. 47, 1817–1826. https://​doi.​org/​10.​1016/j.​eurpo​lymj.​2011.​06.​013 (2011). 10. Hu, W., Wang, Z., Xiao, Y., Zhang, S. & Wang, J. Advances in crosslinking strategies of biomedical hydrogels. Biomater. Sci. 7, 843–855. https://​doi.​org/​10.​1039/​C8BM0​1246F (2019). 11. Li, J. et al. Preparation of conductive composite hydrogels from carboxymethyl cellulose and polyaniline with a nontoxic crosslink- ing agent. RSC Adv. 7, 54823–54828. https://​doi.​org/​10.​1039/​C7RA1​0788A (2017). 12. Han, J., Lei, T. & Wu, Q. Facile preparation of mouldable polyvinyl alcohol-borax hydrogels reinforced by well-dispersed cellulose nanoparticles: physical, viscoelastic and mechanical properties. Cellulose 20, 2947–2958. https://d ​ oi.o ​ rg/1​ 0.1​ 007/s​ 10570-0​ 13-0​ 082- 5 (2013). 13. Parhi, R. Cross-linked hydrogel for pharmaceutical applications: a review. Adv. Pharm. Bull. 7, 515–30. https://​doi.​org/​10.​15171/​ apb.​2017.​064 (2017). 14. Fan, L., Yang, H., Yang, J., Peng, M. & Hu, J. Preparation and characterization of chitosan/gelatin/PVA hydrogel for wound dress- ings. Carbohydr. Polym. 146, 427–434. https://​doi.​org/​10.​1016/j.​carbp​ol.​2016.​03.​002 (2016). 15. Lu, P.-L., Lai, J.-Y., Ma, D.H.-K. & Hsiue, G.-H. Carbodiimide cross-linked hyaluronic acid hydrogels as cell sheet delivery vehicles: characterization and interaction with corneal endothelial cells. J. Biomater. Sci. Polym. Ed. 19, 1–18. https://​doi.​org/​10.​1163/​15685​ 62087​83227​695 (2008). 16. Han, J. et al. Effects of nanocellulose on the structure and properties of poly(vinyl alcohol)-borax hybrid foams. Cellulose 24, 4433–4448. https://​doi.​org/​10.​1007/​s10570-​017-​1409-4 (2017). 17. Han, J., Lei, T. & Wu, Q. High-water-content mouldable polyvinyl alcohol-borax hydrogels reinforced by well-dispersed cellulose nanoparticles: dynamic rheological properties and hydrogel formation mechanism. Carbohydr. Polym. 102, 306–316. https://​doi.​ org/​10.​1016/j.​carbp​ol.​2013.​11.​045 (2014). 18. Leone, G. et al. Poly-vinyl alcohol (PVA) crosslinked by trisodium trimetaphosphate (STMP) and sodium hexametaphosphate (SHMP): effect of molecular weight, pH and phosphorylating agent on length of spacing arms, crosslinking density and water interaction. J. Mol. Struct. 1202, 127264. https://​doi.​org/​10.​1016/j.​molst​ruc.​2019.​127264 (2020). 19. Cagnin, C. et al. Hydrogels of starch/carboxymethyl cellulose crosslinked with sodium trimetaphosphate via reactive extrusion. J. Appl. Polym. Sci. 138, 50194. https://​doi.​org/​10.​1002/​app.​50194 (2021). 20. Ibrahim, A. G., Elkony, A. M. & El-Bahy, S. M. Methylene blue uptake by gum arabic/acrylic amide/3-allyloxy-2-hydroxy-1-pro- panesulfonic acid sodium salt semi-IPN hydrogel. Int. J. Biol. Macromol. 186, 268–277. https://​doi.​org/​10.​1016/j.​ijbio​mac.​2021.​ 07.​033 (2021). 21. Sotolářová, J., Vinter, Š & Filip, J. Cellulose derivatives crosslinked by citric acid on electrode surface as a heavy metal absorption/ sensing matrix. Colloids Surf. A. Physicochem. Eng. Asp. 628, 127242. https://​doi.​org/​10.​1016/j.​colsu​rfa.​2021.​127242 (2021). 22. Lungu, A. et al. Nanocellulose-enriched hydrocolloid-based hydrogels designed using a ­Ca2+ free strategy based on citric acid. Mater. Des. 197, 109200. https://​doi.​org/​10.​1016/j.​matdes.​2020.​109200 (2021). 23. Song, S. et al. Antibacterial polyvinyl alcohol/bacterial cellulose/nano-silver hydrogels that effectively promote wound healing. Mater. Sci. Eng. C. 126, 112171. https://​doi.​org/​10.​1016/j.​msec.​2021.​112171 (2021). 24. Spoljaric, S., Salminen, A., Luong, N. D. & Seppala, J. Stable, self-healing hydrogels from nanofibrillated cellulose, poly(vinyl alcohol) and borax via reversible crosslinking. Eur. Polym. J. 56, 105–117. https://​doi.​org/​10.​1016/j.​eurpo​lymj.​2014.​03.​009 (2014). 25. Sringam, J., Trongsatitkul, T. & Suppakarn, N. Effects of borax and montmorillonite contents on mechanical properties of cassava btarch-based composite hydrogels. AIP Conf. Proc. 2279, 070005. https://​doi.​org/​10.​1063/5.​00229​69 (2020). 26. Thombare, N., Jha, U., Mishra, S. & Siddiqui, M. Z. Borax cross-linked guar gum hydrogels as potential adsorbents for water purification. Carbohydr. Polym. 168, 274–281. https://​doi.​org/​10.​1016/j.​carbp​ol.​2017.​03.​086 (2017). 27. Itou, T., Kitai, H., Shimazu, A., Miyazaki, T. & Tashiro, K. Clarification of cross-linkage structure in boric acid doped poly(vinyl alcohol) and its model compound as studied by an organized combination of X-ray single-crystal structureanalysis, Raman spectroscopy, and density functional theoretical calculation. J. Phys. chem. B. 118, 6032–6037. https://​doi.​org/​10.​1021/​jp502​6569 (2014). 28. Geng, S., Haque, M.M.-U. & Oksman, K. Crosslinked poly(vinyl acetate) (PVAc) reinforced with cellulose nanocrystals (CNC): structure and mechanical properties. Compos. Sci. Technol. 126, 35–42. https://​doi.​org/​10.​1016/j.​comps​citech.​2016.​02.​013 (2016). 29. Lu, B. et al. One-pot assembly of microfibrillated cellulose reinforced PVA–borax hydrogels with self-healing and pH-responsive properties. ACS Sustain. Chem. Eng. 5, 948–956. https://​doi.​org/​10.​1021/​acssu​schem​eng.​6b022​79 (2017). 30. Lin, H. L., Yu, T. L. & Cheng, C. H. Reentrant behavior of poly(vinyl alcohol)–borax semidilute aqueous solutions. Colloid Polym. Sci. 278, 187–194. https://​doi.​org/​10.​1007/​s0039​60050​031 (2000). 31. Tang, L., Feng, Y., He, W. & Yang, F. Combination of graphene oxide with flax-derived cellulose dissolved in NaOH/urea medium to generate hierarchically structured composite carbon aerogels. Ind. Crops Prod. 130, 179–183. https://​doi.​org/​10.​1016/j.​indcr​ op.​2018.​12.​068 (2019). 32. Segal, L., Creely, J. J., Martin, A. E. & Conrad, C. M. An empirical method for estimating the degree of crystallinity of native cel- lulose using the X-ray diffractometer. Text. Res. J. 29, 786–794. https://​doi.​org/​10.​1177/​00405​17559​02901​003 (1959). 33. Duchemin, B., Le Corre, D., Leray, N., Dufresne, A. & Staiger, M. P. All-cellulose composites based on microfibrillated cellulose and filter paper via a NaOH-urea solvent system. Cellulose 23, 593–609. https://​doi.​org/​10.​1007/​s10570-​015-​0835-4 (2016). 34. Wei, Q.-Y. et al. Structure and properties of all-cellulose composites prepared by controlling the dissolution temperature of a NaOH/Urea solvent. Ind. Eng. Chem. Res. 59, 10428–10435. https://​doi.​org/​10.​1021/​acs.​iecr.​9b070​75 (2020). 35. Ghosh, I., Haider, Q. & Sharma, C. Characterization of regenerated cellulose prepared from different pulp grades using a green solvent. Cellul. Chem. Technol. 53, 643–53. https://​doi.​org/​10.​35812/​Cellu​loseC​hemTe​chnol.​2019.​53.​63 (2019). 36. Ou, R. et al. Solid biopolymer electrolytes based on all-cellulose composites prepared by partially dissolving cellulosic fibers in the ionic liquid 1-butyl-3-methylimidazolium chloride. J. Mater. Sci. 47, 5978–5986. https://​doi.​org/​10.​1007/​s10853-​012-​6502-3 (2012). 37. Hildebrandt, N. C., Piltonen, P., Valkama, J. & Illikainen, M. Self-reinforcing composites from commercial chemical pulps via partial dissolution with NaOH/urea. Ind. Crops Prod. 109, 79–84. https://​doi.​org/​10.​1016/j.​indcr​op.​2017.​08.​014 (2017). 38. Dormanns, J. W., Schuermann, J., Müssig, J., Duchemin, B. J. C. & Staiger, M. P. Solvent infusion processing of all-cellulose com- posite laminates using an aqueous NaOH/urea solvent system. Compos. A: Appl. Sci. Manuf. 82, 130–140. https://d ​ oi.o ​ rg/1​ 0.1​ 016/j.​ compo​sitesa.​2015.​12.​002 (2016). 39. Cheng, G. et al. All-cellulose films with excellent strength and toughness via a facile approach of dissolution–regeneration. J. Appl. Polym. Sci. 136, 46925. https://​doi.​org/​10.​1002/​app.​46925 (2019). 40. Ge, W. et al. Rapid self-healing, stretchable, moldable, antioxidant and antibacterial tannic acid-cellulose nanofibril composite hydrogels. Carbohydr. Polym. 224, 115147. https://​doi.​org/​10.​1016/j.​carbp​ol.​2019.​115147 (2019). 41. Lim, M. et al. Highly-enhanced water resistant and oxygen barrier properties of cross-linked poly(vinyl alcohol) hybrid films for packaging applications. Prog. Org. Coat. 85, 68–75. https://​doi.​org/​10.​1016/j.​porgc​oat.​2015.​03.​005 (2015). 42. Tanpichai, S. & Oksman, K. Crosslinked poly(vinyl alcohol) composite films with cellulose nanocrystals: mechanical and thermal properties. J. Appl. Polym. Sci. 135, 45710. https://​doi.​org/​10.​1002/​app.​45710 (2018). Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 10 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) www.nature.com/scientificreports/ 43. Ding, L. et al. Self-healing and acidochromic polyvinyl alcohol hydrogel reinforced by regenerated cellulose. Carbohydr. Polym. 255, 117331. https://​doi.​org/​10.​1016/j.​carbp​ol.​2020.​117331 (2021). 44. Fan, Q. et al. Eco-friendly extraction of cellulose nanocrystals from grape pomace and construction of self-healing nanocomposite hydrogels. Cellulose 27, 2541–2553. https://​doi.​org/​10.​1007/​s10570-​020-​02977-2 (2020). 45. Shao, C. et al. Mimicking dynamic adhesiveness and strain-stiffening behavior of biological tissues in tough and self-healable cellulose nanocomposite hydrogels. ACS Appl. Mater. Interfaces 11, 5885–5895. https://​doi.​org/​10.​1021/​acsami.​8b215​88 (2019). 46. Tanpichai, S. & Witayakran, S. All-cellulose composites from pineapple leaf microfibers: structural, thermal, and mechanical properties. Polym. Compos. 39, 895–903. https://​doi.​org/​10.​1002/​pc.​24015 (2018). 47. Tanpichai, S. & Witayakran, S. All-cellulose composite laminates prepared from pineapple leaf fibers treated with steam explosion and alkaline treatment. J. Reinf. Plast. Compos. 36, 1146–1155. https://​doi.​org/​10.​1177/​07316​84417​704923 (2017). 48. Piltonen, P. et al. Green and efficient method for preparing all-cellulose composites with NaOH/urea solvent. Compos. Sci. Technol. 135, 153–158. https://​doi.​org/​10.​1016/j.​comps​citech.​2016.​09.​022 (2016). 49. Hu, Y., Hu, F., Gan, M., Xie, Y. & Feng, Q. A rapid, green method for the preparation of cellulosic self-reinforcing composites from wood and bamboo pulp. Ind. Crops Prod. 169, 113658. https://​doi.​org/​10.​1016/j.​indcr​op.​2021.​113658 (2021). 50. Qi, H., Yang, Q., Zhang, L., Liebert, T. & Heinze, T. The dissolution of cellulose in NaOH-based aqueous system by two-step process. Cellulose 18, 237–245. https://​doi.​org/​10.​1007/​s10570-​010-​9477-8 (2011). 51. Zhang, J. et al. Improving lignocellulose thermal stability by chemical modification with boric acid for incorporating into poly- amide. Mater. Des. 191, 108589. https://​doi.​org/​10.​1016/j.​matdes.​2020.​108589 (2020). 52. Arévalo, R., Picot, O., Wilson, R. M., Soykeabkaew, N. & Peijs, T. All-cellulose composites by partial dissolution of cotton fibres. J. Biobased Mater. Bioenergy 4, 129–138. https://​doi.​org/​10.​1166/​jbmb.​2010.​1077 (2010). 53. Somseemee, O., Sae-Oui, P. & Siriwong, C. Reinforcement of surface-modified cellulose nanofibrils extracted from Napier grass stem in natural rubber composites. Ind. Crops Prod. https://​doi.​org/​10.​1016/j.​indcr​op.​2021.​113881 (2021). 54. Zhao, D. et al. Dissolution of cellulose in NaOH based solvents at low temperature. Fiber. Polym. 14, 1261–1265. https://​doi.​org/​ 10.​1007/​s12221-​013-​1261-6 (2013). 55. Uddin, K. M. A., Ago, M. & Rojas, O. J. Hybrid films of chitosan, cellulose nanofibrils and boric acid: flame retardancy, optical and thermo-mechanical properties. Carbohydr. Polym. 177, 13–21. https://​doi.​org/​10.​1016/j.​carbp​ol.​2017.​08.​116 (2017). 56. He, S. et al. Bio-inspired lightweight pulp foams with improved mechanical property and flame retardancy via borate cross-linking. Chem. Eng. J. 371, 34–42. https://​doi.​org/​10.​1016/j.​cej.​2019.​04.​018 (2019). 57. Hirata, T. & Werner, K. E. Thermal analysis of cellulose treated with boric acid or ammonium phosphate in varied oxygen atmos- pheres. J. Appl. Polym. Sci. 33, 1533–1556. https://​doi.​org/​10.​1002/​app.​1987.​07033​0510 (1987). 58. Garba, B. & Maduekwe, A. A. L. Mechanistic study of sodium tetraborate decahydrate as flame suppressant for wood cellulose. Int. J. Polym. Mater. Polym. Biomater. 38, 21–35. https://​doi.​org/​10.​1080/​00914​03970​80314​92 (1997). 59. Wicklein, B., Kocjan, D., Carosio, F., Camino, G. & Bergström, L. Tuning the nanocellulose–borate interaction to achieve highly flame retardant hybrid materials. Chem. Mater. 28, 1985–1989. https://​doi.​org/​10.​1021/​acs.​chemm​ater.​6b005​64 (2016). 60. Uyanga, K. A. & Daoud, W. A. Green and sustainable carboxymethyl cellulose-chitosan composite hydrogels: effect of crosslinker on microstructure. Cellulose 28, 5493–5512. https://​doi.​org/​10.​1007/​s10570-​021-​03870-2 (2021). 61. Tanpichai, S. & Oksman, K. Cross-linked nanocomposite hydrogels based on cellulose nanocrystals and PVA: mechanical proper- ties and creep recovery. Compos. A: Appl. Sci. Manuf. 88, 226–233. https://​doi.​org/​10.​1016/j.​compo​sitesa.​2016.​06.​002 (2016). 62. Zainul Armir, N. A., Mohd Salleh, K., Zulkifli, A. & Zakaria, S. pH-responsive ampholytic regenerated cellulose hydrogel integrated with carrageenan and chitosan. Ind. Crops Prod. 178, 114588. https://​doi.​org/​10.​1016/j.​indcr​op.​2022.​114588 (2022). 63. Zhang, L. et al. High strength graphene oxide/polyvinyl alcohol composite hydrogels. J. Mater. Chem. A. 21, 10399–10406. https://​ doi.​org/​10.​1039/​c0jm0​4043f (2011). 64. Aydınoğlu, D. Investigation of pH-dependent swelling behavior and kinetic parameters of novel poly(acrylamide-co-acrylic acid) hydrogels with spirulina. E-Polym. 15, 81–93. https://​doi.​org/​10.​1515/​epoly-​2014-​0170 (2015). 65. Sheikhi, M., Rafiemanzelat, F., Moroni, L. & Setayeshmehr, M. Ultrahigh-water-content biocompatible gelatin-based hydrogels: toughened through micro-sized dissipative morphology as an effective strategy. Mater. Sci. Eng. C. 120, 111750. https://​doi.​org/​ 10.​1016/j.​msec.​2020.​111750 (2021). 66. Qin, Y., Liu, Y., Yuan, L., Yong, H. & Liu, J. Preparation and characterization of antioxidant, antimicrobial and pH-sensitive films based on chitosan, silver nanoparticles and purple corn extract. Food Hydrocoll. 96, 102–111. https://​doi.​org/​10.​1016/j.​foodh​yd.​ 2019.​05.​017 (2019). 67. Drozdov, A. D. & Declaville Christiansen, J. The effects of pH and ionic strength on equilibrium swelling of polyampholyte gels. Int. J. Solids and Struct. 110–111, 192–208. https://​doi.​org/​10.​1016/j.​ijsol​str.​2017.​01.​028 (2017). 68. Schott, H. Swelling kinetics of polymers. J. Macromol. Sci. B. 31, 1–9. https://​doi.​org/​10.​1080/​00222​34920​82154​53 (1992). 69. Sayyed, A. J., Mohite, L. V., Deshmukh, N. A. & Pinjari, D. V. Swelling kinetic study with mathematical modeling of cellulose pulp in aqueous N-methyl-morpholine-N-oxide solution. React. Kinet. Mech. Catal. 133, 101–115. https://d ​ oi.o ​ rg/1​ 0.1​ 007/s​ 11144-0​ 21-​ 02000-0 (2021). 70. Barus, D. A., Humaidi, S., Ginting, R. T. & Sitepu, J. Enhanced adsorption performance of chitosan/cellulose nanofiber isolated from durian peel waste/graphene oxide nanocomposite hydrogels. Environ. Nanotechnol. Monit. Manag. 17, 100650. https://​doi.​ org/​10.​1016/j.​enmm.​2022.​100650 (2022). 71. Yilmaz, M. T. Minimum inhibitory and minimum bactericidal concentrations of boron compounds against several bacterial strains. Turk. J. Med. Sci. 42, 1423–1429. https://​doi.​org/​10.​3906/​sag-​1205-​83 (2012). Acknowledgements The authors are grateful to Thailand Science research and Innovation Fund Chulalongkorn University (CU_ FRB65_bcg (15)_083_23_13) for financial support and Faculty of Science, Chulalongkorn University for instru- mental support. Moreover, this project is funded by National Research Council of Thailand (NRCT) (Grant No. N41A640090). One of the authors (S. Tanpichai) would like to thank Thailand Toray Science Foundation for the financial support of the science and technology research grant and TunTun for helping his parents to take care of his little brother, Monty, during COVID-19 pandemic. Author contributions S.T.: Conceptualization, Methodology, Investigation, Project administration, Supervision, Visualization, Writ- ing—original draft preparation, Writing—review and editing. F.P.: Data curation; Formal analysis; Validation. A.B.: Conceptualization, Methodology, Investigation, Resources, Supervision Writing—original draft preparation. Competing interests The authors declare no competing interests. Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 11 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol.:(0123456789)  www.nature.com/scientificreports/ Additional information Correspondence and requests for materials should be addressed to A.B. Reprints and permissions information is available at www.nature.com/reprints. Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://​creat​iveco​mmons.​org/​licen​ses/​by/4.​0/. © The Author(s) 2022 Scientific Reports | (2022) 12:8920 | https://doi.org/10.1038/s41598-022-12688-2 12 Content courtesy of Springer Nature, terms of use apply. Rights reserved Vol:.(1234567890) Terms and Conditions Springer Nature journal content, brought to you courtesy of Springer Nature Customer Service Center GmbH (“Springer Nature”). Springer Nature supports a reasonable amount of sharing of research papers by authors, subscribers and authorised users (“Users”), for small- scale personal, non-commercial use provided that all copyright, trade and service marks and other proprietary notices are maintained. By accessing, sharing, receiving or otherwise using the Springer Nature journal content you agree to these terms of use (“Terms”). For these purposes, Springer Nature considers academic use (by researchers and students) to be non-commercial. These Terms are supplementary and will apply in addition to any applicable website terms and conditions, a relevant site licence or a personal subscription. These Terms will prevail over any conflict or ambiguity with regards to the relevant terms, a site licence or a personal subscription (to the extent of the conflict or ambiguity only). For Creative Commons-licensed articles, the terms of the Creative Commons license used will apply. We collect and use personal data to provide access to the Springer Nature journal content. We may also use these personal data internally within ResearchGate and Springer Nature and as agreed share it, in an anonymised way, for purposes of tracking, analysis and reporting. We will not otherwise disclose your personal data outside the ResearchGate or the Springer Nature group of companies unless we have your permission as detailed in the Privacy Policy. While Users may use the Springer Nature journal content for small scale, personal non-commercial use, it is important to note that Users may not: 1. use such content for the purpose of providing other users with access on a regular or large scale basis or as a means to circumvent access control; 2. use such content where to do so would be considered a criminal or statutory offence in any jurisdiction, or gives rise to civil liability, or is otherwise unlawful; 3. falsely or misleadingly imply or suggest endorsement, approval , sponsorship, or association unless explicitly agreed to by Springer Nature in writing; 4. use bots or other automated methods to access the content or redirect messages 5. override any security feature or exclusionary protocol; or 6. share the content in order to create substitute for Springer Nature products or services or a systematic database of Springer Nature journal content. In line with the restriction against commercial use, Springer Nature does not permit the creation of a product or service that creates revenue, royalties, rent or income from our content or its inclusion as part of a paid for service or for other commercial gain. Springer Nature journal content cannot be used for inter-library loans and librarians may not upload Springer Nature journal content on a large scale into their, or any other, institutional repository. These terms of use are reviewed regularly and may be amended at any time. Springer Nature is not obligated to publish any information or content on this website and may remove it or features or functionality at our sole discretion, at any time with or without notice. Springer Nature may revoke this licence to you at any time and remove access to any copies of the Springer Nature journal content which have been saved. To the fullest extent permitted by law, Springer Nature makes no warranties, representations or guarantees to Users, either express or implied with respect to the Springer nature journal content and all parties disclaim and waive any implied warranties or warranties imposed by law, including merchantability or fitness for any particular purpose. Please note that these rights do not automatically extend to content, data or other material published by Springer Nature that may be licensed from third parties. If you would like to use or distribute our Springer Nature journal content to a wider audience or on a regular basis or in any other manner not expressly permitted by these Terms, please contact Springer Nature at [email protected]