Manufacturing Processes PDF

 This page intentionally left blank MANUFACTURING PROCESSES (SECOND EDITION) H.N. Gupta B.Sc., G.I. Mech.E (London), FIE Visiting Professor Department of Mechanical Engineering I.E.T., Lucknow, U.P. Technical University R.C. G...

 This page intentionally left blank MANUFACTURING PROCESSES (SECOND EDITION) H.N. Gupta B.Sc., G.I. Mech.E (London), FIE Visiting Professor Department of Mechanical Engineering I.E.T., Lucknow, U.P. Technical University R.C. Gupta B.Sc., B.E., M.Tech., Ph.D. Professor and Head Department of Mechanical Engineering I.E.T., Lucknow, U.P. Technical University Arun Mittal Senior Faculty Department of Mechanical Engineering I.E.T., Lucknow, U.P. Technical University Copyright © 2009, New Age International (P) Ltd., Publishers Published by New Age International (P) Ltd., Publishers All rights reserved. No part of this ebook may be reproduced in any form, by photostat, microfilm, xerography, or any other means, or incorporated into any information retrieval system, electronic or mechanical, without the written permission of the publisher. All inquiries should be emailed to [email protected] ISBN (13) : 978-81-224-2844-5 PUBLISHING FOR ONE WORLD NEW AGE INTERNATIONAL (P) LIMITED, PUBLISHERS 4835/24, Ansari Road, Daryaganj, New Delhi - 110002 Visit us at www.newagepublishers.com  Preface to the Second Edition The authors of the book ‘‘Manufacturing Processes’’ are thrilled at the speed with which the first edition of the book has been snapped up and exhausted within four months of its publication necessitating a reprint. This proves that the book has been found useful both by teachers and the students. This is extremely gratifying. It has been felt that to make the text of the book even more useful, certain changes have been made. Therefore the text of the Unit I and Unit IV has been completely rewritten in the second edition of the book. However, the essential features of the book have not been altered. The text is in simple narrative style and does not presume any preliminary knowledge of the subject matter. The text is neither too detailed, nor has any essential information been left out. The text is amply illustrated. To make the book even more useful, the question bank has been widened and a number of questions of objective type have been added unitwise at the end of each unit. It is the author’s belief that this second edition of the book will be found extremely useful by both the faculty and the students. AUTHORS 10D\N-MANU\TIT-MA.PM5 II  This page intentionally left blank  Preface to the First Edition The ‘driving force’ behind a ‘technological revolution’ has always been a certain ‘material’. There would have been no ‘industrial revolution’ without ‘steel’ and no ‘electronic/computer revolution’ without ‘semiconductor’. Similary the ‘key’ behind ‘socioeconomic development’ is the ‘manufacturing’ which is done by certain manufacturing processes using certain materials. Moreovers, the primary duty of engineers is to make life-style of people more easy and comfortable, engineers do this by ‘making’ certain tools and things through certain manufacturing processes using certain material of desirable property. The present book on ‘Manufacturing Processes’ is what every engineer, irrespective of branch or specialization, should know. Note that this book is not a book on ‘Workshop’ Technology’. ‘Workshop Technology’ is usually taught as ‘Workshop-Practice’ usually with 0-1-3. L-T-P, meaning by 3-lab hours and 1 hour for tutorial (or lecture) for the theory of workshop tools & processes. The book on ‘Manufacturing Processes’ covers a wide overview of ‘material’, manufacturing processes’ and other ‘misc. topics’. Unit-I deals with Basic-Metals & alloys: Properties and Applications. Units-II and III cover major manufacturing processes such as Metal Forming & Casting and Machining & Welding. The last Unit-IV covers misc. and left-over but relevant topics. The details of topics are given in the syllabus and on the content pages. The book is intended for engineers of any specialization to present an overview of manufacturing process and the material used in it. The book would be useful as a core-course to B.Tech. students of all branches and all universities throughout the world. The book is considered to be useful universally, specially in view of syllabus of ‘Manufacturing Processes. AUTHORS 10D\N-MANU\TIT-MA.PM5 I  This page intentionally left blank  Contents Preface to the Second Edition..................................................................................................... v Preface to the First Edition........................................................................................................ vii Unit I BASIC METALS AND ALLOYS : PROPERTIES AND APPLICATIONS 1 PROPERTIES OF MATERIALS 3–10 Introduction................................................................................................................................... 3 Properties of Materials................................................................................................................... 3 Stress-Strain Diagram.................................................................................................................... 3 Malleability and Ductility................................................................................................................ 6 Brittleness...................................................................................................................................... 6 Stiffness and Resilience................................................................................................................. 6 Toughness and Impact Strength................................................................................................... 6 Hardness........................................................................................................................................ 7 Fracture of Material....................................................................................................................... 8 Fatigue Failure............................................................................................................................... 9 Creep Failure.................................................................................................................................. 9 Questions................................................................................................................................. 10 2 FERROUS MATERIALS 11–18 Introduction................................................................................................................................. 11 Iron and Steel............................................................................................................................... 11 Classification of Steels................................................................................................................. 11 Wrought Iron............................................................................................................................... 13 Cast Iron...................................................................................................................................... 13 Alloy Steels.................................................................................................................................. 15 Heat Treatment of Carbon Steels................................................................................................ 17 Questions..................................................................................................................................... 18 3 NON-FERROUS METALS AND ALLOYS 19–25 Introduction................................................................................................................................. 19 Properties and Uses of Non-Ferrous Metals............................................................................... 19 Alloys of Copper.......................................................................................................................... 20 Cupro-Nickels.............................................................................................................................. 22 Aluminium Alloys......................................................................................................................... 22 Alloys of Nickel........................................................................................................................... 22 Questions..................................................................................................................................... 23 Objective Type Questions....................................................................................................... 24-25 Unit II INTRODUCTION TO METAL FORMING AND CASTING PROCESS 1 BASIC METAL FORMING PROCESSES AND USES 29–33 Introduction................................................................................................................................. 29 Advantages of Mechanical Working Processes.......................................................................... 29 Difference Between Hot and Cold Working................................................................................ 30 Advantages and Disadvantages of Cold and Hot Working Processes......................................... 31 Classification of Metal Forming Processes According to Type of Stress Employed................. 32 Questions..................................................................................................................................... 33 2 FORGING 34–44 Introduction................................................................................................................................. 34 Classification of Forging.............................................................................................................. 34 Die Forging with Power Hammers............................................................................................. 40 Open Die Forging........................................................................................................................ 40 Impression Die Forging............................................................................................................... 41 Closed Die Forging...................................................................................................................... 41 Drop Stamping or Drop Forging Hammers................................................................................ 41 Some Important Considerations Leading to Sound Forgings..................................................... 42 Forging Presses........................................................................................................................... 42 Machine Forging.......................................................................................................................... 42 Forging Defects........................................................................................................................... 43 Heat Treatment of Forgings........................................................................................................ 43 Cold Forging................................................................................................................................ 44 Questions..................................................................................................................................... 44 3 ROLLING 45–56 Introduction................................................................................................................................. 45 Nomenclature of Rolled Products............................................................................................... 46 Mechanism of Rolling.................................................................................................................. 46  Types of Rolling Mills.................................................................................................................. 48 Rolls and Roll Pass Design.......................................................................................................... 50 Ring Rolling................................................................................................................................. 51 Cold Rolling................................................................................................................................. 52 Rolling Defects............................................................................................................................ 53 Questions..................................................................................................................................... 56 4 EXTRUSION, WIRE DRAWING, TUBE DRAWING AND MAKING 57–65 Extrusion Processes.................................................................................................................... 58 Machines for Extrusion............................................................................................................... 62 Extrusion Defects........................................................................................................................ 62 Wire Drawing............................................................................................................................... 62 Tube Drawing.............................................................................................................................. 63 Tube Making................................................................................................................................ 64 Questions..................................................................................................................................... 65 5 PRESS WORK AND DIE-PUNCH ASSEMBLY 66–72 Tools............................................................................................................................................ 66 Other Operations Performed with Presses.................................................................................. 68 Bending........................................................................................................................................ 68 Deep Drawing.............................................................................................................................. 69 Coining and Embossing............................................................................................................... 70 Coining......................................................................................................................................... 70 Guillotine Shear............................................................................................................................ 71 Questions..................................................................................................................................... 72 6 CASTING PROCESS 73–85 Introduction................................................................................................................................. 73 Patterns........................................................................................................................................ 74 Pattern Allowances...................................................................................................................... 74 Types of Patterns......................................................................................................................... 74 Moulding Sand and its Properties................................................................................................ 76 Mould Making Technique............................................................................................................ 77 Cores............................................................................................................................................ 79 Core Prints................................................................................................................................... 79 Gates, Runners and Risers.......................................................................................................... 80 Cupola.......................................................................................................................................... 81 Construction................................................................................................................................ 81 Operation of Cupola..................................................................................................................... 82 Casting Defects........................................................................................................................... 82 Die Casting................................................................................................................................... 83  Steps in Die Casting..................................................................................................................... 84 Questions..................................................................................................................................... 85 Objective Type Questions...................................................................................................... 86–87 Unit III INTRODUCTION TO MACHINING AND ITS APPLICATIONS 1 LATHE 91–99 Introduction................................................................................................................................. 91 Centre Lathe................................................................................................................................. 92 Cutting Tools Used on the Lathe................................................................................................. 94 Holding the Work Piece in the Chuck and Centering.................................................................. 95 Taper Turning.............................................................................................................................. 96 Profile or Form Turning.............................................................................................................. 98 Questions..................................................................................................................................... 99 2 SHAPERS AND PLANERS 100–105 Introduction............................................................................................................................... 100 Shaping Machines or Shaper..................................................................................................... 100 Drive.......................................................................................................................................... 101 Cutting Tools Used in Shaping.................................................................................................. 102 Operations Performed on Shapers............................................................................................ 102 Planer or Planning Machine....................................................................................................... 104 Principle of Working.................................................................................................................. 104 Questions................................................................................................................................... 105 3 DRILLING MACHINES 106–110 Twist Drill.................................................................................................................................. 106 Drilling Machines....................................................................................................................... 107 Questions................................................................................................................................... 110 4 MILLING PROCESS 111–119 Introduction................................................................................................................................ 111 Basic Milling Process.................................................................................................................. 111 Types of Milling Processes........................................................................................................ 112 Peripheral Milling....................................................................................................................... 113 Face Milling............................................................................................................................... 115 End Milling................................................................................................................................. 116 Milling Machines........................................................................................................................ 117 Horizontal Milling Machine........................................................................................................ 117 Questions................................................................................................................................... 119 5 GRINDING PROCESS 120–126 Introduction............................................................................................................................... 120 Choice of Abrasives................................................................................................................... 120 Classification of Wheels............................................................................................................ 121 Grit............................................................................................................................................. 121 Bond and Grade......................................................................................................................... 121 Wheel Structure......................................................................................................................... 121 Wheel Shapes............................................................................................................................. 122 Mounting a Wheel on Machine, Balancing, Truing and Dressing............................................. 123 Grinding Operations and Grinding Machines............................................................................ 123 Coolant....................................................................................................................................... 126 Questions................................................................................................................................... 126 6 WELDING PROCESS 127–141 Classification.............................................................................................................................. 127 Gas Welding Process................................................................................................................. 127 Equipment Needed for Gas Welding......................................................................................... 128 Types of Flames........................................................................................................................ 130 Welding Operation..................................................................................................................... 130 Use of Filler Rods and Fluxes................................................................................................... 133 Oxyacetylene Cutting................................................................................................................. 133 Arc Welding............................................................................................................................... 133 Striking an Arc........................................................................................................................... 134 Heat Affected Zone.................................................................................................................... 135 Arc Blow.................................................................................................................................... 135 Welding Positions....................................................................................................................... 135 Arc Welding Defects.................................................................................................................. 136 Electric Resistance Welding....................................................................................................... 136 Soldering and Brazing................................................................................................................ 140 Soldering Process...................................................................................................................... 140 Brazing Process......................................................................................................................... 140 Questions................................................................................................................................... 141 Objective Type Questions.................................................................................................. 142–143 Unit IV MISCELLANEOUS TOPICS 1 IMPORTANCE OF MATERIALS AND MANUFACTURING 147–153 Introduction............................................................................................................................... 147 Proper Selection of Material...................................................................................................... 147 Importance of Materials............................................................................................................ 148  Historical Perspective................................................................................................................ 149 Materials as Driving-Force Behind Technological Developments............................................. 149 Direct and Indirect Linkages Among Materials, Manufacturing, Technological Development and Socioeconomic Improvement............................................... 152 Conclusion................................................................................................................................. 152 Questions................................................................................................................................... 153 2 LOCATION AND LAYOUT OF PLANTS, PRODUCTION AND PRODUCTIVITY 154–157 Introduction............................................................................................................................... 154 Location of Plants...................................................................................................................... 154 Layout of Plants......................................................................................................................... 155 Advantages of a Good Layout................................................................................................... 155 Types of Layouts....................................................................................................................... 155 Types of Production.................................................................................................................. 156 Production and Productivity...................................................................................................... 157 Questions................................................................................................................................... 157 3 NON-METALLIC MATERIALS 158–167 Common Types and Uses of Wood........................................................................................... 158 Uses of Wood............................................................................................................................ 159 Cement Concrete....................................................................................................................... 159 Ceramics.................................................................................................................................... 160 Rubbers...................................................................................................................................... 160 Plastics....................................................................................................................................... 162 Composite Materials.................................................................................................................. 165 Questions................................................................................................................................... 167 4 MISCELLANEOUS PROCESSES 168–173 Powder Metallurgy Process...................................................................................................... 168 Plastic Products Manufacturing Processes............................................................................... 169 Galvanising Process................................................................................................................... 171 Electroplating Process............................................................................................................... 172 Faraday’s Laws of Electrolysis................................................................................................. 173 Questions................................................................................................................................... 173 Objective Type Questions.................................................................................................. 174–175 QUESTION PAPER 177–179  UNIT I Basic Metals and Alloys : Properties and Applications  This page intentionally left blank  +0)26-4  Properties of Materials INTRODUCTION Materials are the driving force behind the technological revolutions and are the key ingredients for manu- facturing. Materials are everywhere around us, and we use them in one way or the other. The materials and the manufacturing process employed, could be better appreciated if one understands various types of materials and its properties. PROPERTIES OF MATERIALS Properties of materials include mechanical properties (such as strength, hardness, toughness), thermal properties (conductivity), optical properties (refractive index), electrical properties (resistance) etc. Here, however, we shall concentrate only on mechanical properties which are most important in manufacturing processes and also in everyday life and we use these terms quite often. To understand the mechanical properties, it is useful to first understand the behaviour of the material when subjected to a force which causes deformation; this could be understood with the ‘stress-strain diagram’. STRESS-STRAIN DIAGRAM Consider a rod of initial length L0 and area A0 which is subjected to a load F. The stress σ is the force per unit area, and strain ε is the change in length (δ) divided by the initial length. Thus, Stress σ = F/A0 Strain ε = δ/L0 The σ-ε curve for a material (say mild steel) is shown in the Fig. 1.1. Up to the proportionality point A, the stress-strain variation is linear. Up to this point Hooke’s law holds good. i.e., σ∝ε or σ = Eε where E is the Young’s modulus commonly called modulus of elasticity. Beyond point A and up to point B, material remains elastic i.e., the material returns to its original condition of the forces acting on it is removed. 3  4 Manufacturing Processes E F C B A D A is limit of proportionality Stress, (σ) B is elastic limit C is upper yield point D is lower yield point E represents ultimate tensile stress F is breaking point O Strain, (ε) Fig. 1.1 Stress-strain curve for ductile material If the specimen is stressed beyond point B, permanent set takes place and we enter plastic defor- mation region. In the plastic deformation region, the strain does not get fully removed even with the removal of the force causing it. If the force is increased further, point ‘C’ is reached where the test specimen stretches even when the stress is not increased. This point is called yield point. Infact, there are two yield points C and D which are called upper and lower yield points respectively. With further straining, the effect of a phenomenon called strain hardening or work hardening takes place.* The material becomes stronger and harder and its load bearing capacity increases. The test specimen is therefore able to bear more stress. On progressively increasing the force acting on the specimen, point E is reached. This point is the highest point in the stress-strain curve and represents the point of maximum stress. It is, therefore, called ultimate tensile strength (UTS) of the material. It is equal to the maximum load applied divided by the original cross-sectional area (A0) of the test specimen. Here, we must consider the effect of increasing load on the cross-sectional area of the test specimen. As plastic deformation increases, the cross-sectional area of the specimen decreases. However for calculation of the stress in the stress-strain graph, the original cross-sectional area is considered. It is for this reason, that the point of breakage F seems to occur at a lower stress level than the UTS point E. After UTS point E, a sharp reduction in cross-sectional area of the test specimen takes place and a “neck” is formed in the centre of the specimen. Ultimately the test specimen breaks in two pieces as the neck becomes thinner and thinner. The actual breaking stress is much higher than the UTS, if the reduced cross-sectional area of the test specimen is taken into account. The measure of the strength of a material is the ultimate tensile strength (σ at point E). However, from the point of view of a design engineer, the yield point is more important as the structure designed by him should withstand forces without yielding. Usually yield stress (σ at point D) is two-thirds of the UTS and this is referred to as yield-strength of the material. In actual practice, to determine UTS, a tensile test is carried out on a tensile testing or a universal *This phenomenon is more fully described in Unit II, Chapter 1. Properties of Materials 5 testing machine. In order that tests conducted in different laboratories on the same material may give identical test results, the test piece used for the tensile test has been standardised. A standard test piece is shown in Fig. 1.2. 20 φ 30 25 30 R 23 φ 25 φ Gauge length Shoulder length Overall length Note: Gauge, shoulder and overall lengths according to IS : 210-1978. Fig. 1.2 Dimensions of a standard tensile test-piece A stress-strain curve for brittle material is obtained by subjecting a test bar of such material in a tensile testing machine. The tensile load is gradually increased and the extention of the test piece is recorded. The stress-strain curve for a brittle material shows some marked differences as compared to the curve obtained for a ductile material. A typical stress-strain curve for a brittle material is shown in Fig. 1.3. Breaking point Tensile stress Strain Fig. 1.3 Stress-strain curve for brittle material This curve displays no yield point, and the test specimen breaks suddenly without any appreci- able necking or extension. In the absence of a yield point, concept of “proof-stress” has been evolved for measuring yield strength of a brittle material. For example, 0.2% proof-stress indicates the stress at which the test specimen ‘suffers’ a permanent elongation equal to 0.2% of initial gauge length and is denoted by σ0.2. The tensile test and the stress-strain curve has been described above in some detail, because a lot of useful information with regard to other properties of material can be gleaned from it. It may be noted that most tensile testing machines are provided with equipment to carry out a compressive strength test as well.  6 Manufacturing Processes MALLEABILITY AND DUCTILITY Both these properties relate to the plasticity of the material. Malleability refers to the ability of plastic deformation under compressive loads, while ductility refers to plastic deformation under tensile loads. A malleable material can be beaten into thin sheets and even thinner foils. A ductile material can be drawn into wires. A measure of ductility is “percentage elongation”. Before the tensile test begins two punch marks are made on the stem of the tensile test piece. Distance between these marks is noted and is known as gauge length (l0). After the tensile test piece fractures in two pieces, the two pieces are retrieved and placed together as close to each other as possible. Now the distance between the two punch marks is measured and noted again. Let this distance be l1. The % elongation is calculated as l1 − l0 × 100 l0 High values of percentage elongation indicate that material is very ductile. Low values indicate that material is brittle and has low ductility. For mild steel, the percentage elongation usually is 20% or more. BRITTLENESS Brittleness can be thought of as opposite of ductility. It is a property which is possessed in great meas- ure by glass and other ceramics. A piece of glass, if dropped on a hard surface shatters and is broken in many pieces. The real cause of brittleness is inability of the material to withstand shock loads. Of course, glass is an extreme case of brittle material. STIFFNESS AND RESILIENCE A material with high value of modulus of elasticity is said to be stiff and a material with low value of modulus of elasticity is said to be resilient. Consider a material undergoing tensile stress within the elastic range. If the material possesses a high value of Young’s modulus (which is the modulus of elasticity corresponding to tensile stress), the material will not stretch much. It will behave as a “stiff ” material. In this case, the slope of the line OA (Fig. 1.1) will be more. Resilience is a property which is totally opposite to stiffness. A beam made of stiff material will deflect to a lesser extent as compared to another made of resilient material under identical loading condition. TOUGHNESS AND IMPACT STRENGTH Toughness and impact strength are allied or similar properties (although these are some differences as mentioned later). They represent the ability of the material to absorb energy before actual failure/ fracture occurs. Refer to Fig. 1.1. If the scale of y-axis is changed and if force is plotted on this axis and, if actual elongation is plotted on x-axis instead of strain, we shall obtain a force-elongation curve instead of stress-strain curve. The shape of curve will remain the same; only scales of x and y axes will change. Now the area under this curve will represent energy required to fracture the material. Higher Properties of Materials 7 the energy, higher is the toughness of material. Toughness comes from a combination of strength and percentage elongation. Since this property enables a material to withstand both elastic and plastic strains, it is considered very important. Higher impact strength goes with higher toughness. In actual impact testing, loads used are dynamic loads and the load is directed to the specimen through a sharp notch. Two tests have been standardised to measure the impact strength of a material (as also its toughness). These tests are called (i) IZOD test, and (ii) Charpy test. IZOD test is described below in brief. A standardised test specimen is shown below in Fig. 1.4 (a). Test specimen Direction of blow 45° 2 mm V notch 28 mm Specimen 10 mm clamped 75 mm in testing square machine Fig. 1.4 (a) IZOD test specimen Fig. 1.4 (b) Specimen fixed in IZOD testing machine This specimen is fixed in the IZOD testing machine in a vertical position as shown in Fig. 1.4 (b). A blow from a swinging pendulum falling from a specified height is then struck on the test specimen 22 mm above the notch. The mass of the pendulum is known. Since height from which pendulum descends down to strike the blow is also known, we know the energy stored in the pendulum (m.g.h.). After striking the test piece and fracturing it at the notch, the pendulum moves on and the height to which it rises on the otherside of the test piece is noted and measured. Thus the energy still left in the pendulum can be calculated. The difference between the original energy in the pendulum and the energy left over after breaking the test specimen is assumed to have been used up in breaking the test specimen. This is taken as the impact strength of the material of the specimen. A correction factor for friction at pendulum bearing is applied to get accurate result. A brittle material has low impact strength and poor toughness. HARDNESS Hardness is a very important property of materials. Hardness indicates wear-resistance and resistance against abrasion or scratching. A hard material also offers resistance to penetration by another body. In the olden days, a scale of hardness was established and diamond, which is the hardest known material was put on top of this scale. Glass and other materials were put lower down on this scale. The criterion used was a simple scratch test. If a material could scratch another material, then the former was considered harder than the latter material and was placed higher in the scale of hardness.  8 Manufacturing Processes In modern times, several tests for hardness have been devised. The most popular ones are called (i) Brinell hardness test, (ii) Rockwell hardness test, and (iii) Vicker’s hardness test. All these tests are based on resistance of the material under test against penetration by a specially designed and manufac- tured “indentor” into the surface of the test specimen under specified load. A harder material offers more resistance and therefore the indentor cannot penetrate its surface to the same depth as it would, if the test specimen were of softer material. Thus the depth of the impression made by the indentor into the test specimen or the area of the impression left by the indentor into the specimen is used to measure the hardness of the material. It is beyond the scope of this book to give detailed test procedures. However, the essential information is given in Table 1.1. Table 1.1 Brinell test Rockwell test Vicker’s test Indentor used Hardened steel ball of 10 mm A diamond cone, called A square based diamond diameter. brale is used. pyramid containing an angle of 136° between opposite faces. Load applied 3000 kg for 10–15 seconds Load is applied in two 5 kg–120 kg. on the indentor stages. First a minor load of during test 10 kg followed by major load of 150 kg, in case of ‘C’ scale. How is hard- Load on ball (kg) Rockwell hardness No. VPN or VHN BHN = Area of ball impression Load ness number in mm 2 = 100 – 500 t, where t is = Area of impression calculated depth of indentation. Special Depending upon material 1. There are several hard- In practice VPN is not cal- comment to be tested, dia of ball and ness scales used like A, B, C culated. The indentation left load applied may change etc. They are meant for by the diamond pyramid is in different materials. The the shape of a rectangle. The major load applied and even lengths of its diagonals the indentor may change. is measured and VPN directly 2. Hardness is never calcu- found from a table against the lated. The hardness no. is measured value of diagonal. read off a graduated dial. 3. For ferrous material we generally use ‘C’ scale. FRACTURE OF MATERIAL If a specimen is subjected to high stress beyond its strength, it fails and ultimately fractures in two or more parts. During the description of the tensile test, we have already come across fractures of ductile and brittle material. The ductile fracture occur after considerable plastic deformation and shows a Properties of Materials 9 characteristic reduction in the cross-sectional area near the fractured portion. Brittle fracture occurs suddenly when a small crack in the cross-section of the material grows resulting in a complete fracture. But such fracture does not show much plastic deformation. Actually, by a careful examination of the fractured surface and the macro and micro metallurgical examination of the fractured specimen, much interesting information as to the probable cause of its failure can be deduced by an experienced metallurgist. Apart from the ductile and brittle type of fractures, we also have fractures caused by FATIGUE and CREEP of material. FATIGUE FAILURE It has been noticed that materials often fail or fracture at a stress level far below their strength, if the stress is either (i) alternating type or (ii) it is varying periodically. What is meant by alternating stress? An example will make this clear. Consider an axle fitted with two wheels. The axle bears the weight of the vehicle and at the same time it rotates along with wheels. Because of weight, the axle under goes a little deflection causing compressive stress in its top half and tensile stress in bottom half of the cross- section. But since it is rotating, with every 180° rotation, the bottom half becomes the top half and vice versa. Thus the nature of stress at any point in the axle keep alternating between compression and tension due to its rotation. A varying stress cycle means that the magnitude of the stress keeps reducing and increasing periodically although its sign does not change. If the material is subjected to several million cycles of either the alternating or varying stress, it gets fatigued and fails even though the magnitude of such stresses may be far lower as compared to its strength. Fortunately, there is a level of alternating and varying stress, which the material is able to withstand without failure even if it is subjected to infinite number of cycles. This is called the ENDURANCE LIMIT. A designer ensures that a component subject to fatigue in service is so designed that its actual stress level remains below the endurance limit. The visual examination of a fatigue fracture shows three distinct zones. These are: (i) The point of crack initiation, it is the point from where the crack may have originated e.g. a notch like a key way or some materials defect like an impurity, or even a surface blemish. (ii) The area of crack propagation during service. This area is usually characterised by circular ring-like scratch marks with point of crack initiation as the centre. (iii) Remaining area of cross-section showing signs of sudden breakage. As a result of crack propagation with time, a stage comes, when the remaining cross-sectional area becomes too small to sustain the stress and fractures suddenly. CREEP FAILURE Failure of material can take place even under steady loads within the strength of the material. This happens if the subjected components remain under steady loads for a very longtime especially when they are subjected to high temperature conditions. Some common examples are stays in boilers, steam  10 Manufacturing Processes turbine blades, furnace parts etc. Such failures are termed creep-failures due to the fact the material continues to deform plastically under such conditions although at a very very slow rate. But over long periods of time, the effect of creep can become appreciable resulting in ultimate failure of the component. QUESTIONS 1. Draw a stress-strain curve for a ductile material. In what respects, a similar curve for a brittle material will be different? 2. What do you understand by the following terms ? (i) Limit of proportionality (ii) Yield-point (iii) Ultimate tensile strength. 3. Explain the meaning of the following terms: (i) Stiffness, (ii) Toughness, and (iii) Hardness. 4. Differentiate between failure of material due to fatigue and creep. 5. What do you understand by percentage elongation? What does a high percentage elongation value signify? 6. Name three common ‘‘hardness’’ tests. Describe anyone of them.  +0)26-4 Ferrous Materials INTRODUCTION Ferrous material refers to those materials whose main constituent is iron; while non-ferrous materials are those which do not contain iron in any appreciable quantity. Ferrous materials are usually stronger and harder and are used extensively in our daily lives. One very special property of ferrous materials is that, their properties can be significantly altered by heat treatment processes or by addition of small quantities of alloying elements. Ferrous materials are relatively cheap but suffer from a great disadvantage. They are subject to corrosion and rusting. IRON AND STEEL Most common engineering materials are ferrous materials such as mild steel and stainless steel which are alloys of iron. It is truly said that gold is metal for kings and iron is king of metals. Otto Von Bismark of Germany once said that “for development of a nation, lectures and meetings are not important, but what is important are blood and steel”. Incidentally, what is common in blood and steel is “iron’’. Though iron is important, but it is mostly used in the form of its alloy, namely steel. To a layman, words iron and steel convey the same meaning. But iron and steel are two different things. Iron is the name given to the metal, whose chemical symbol is Fe and refers to pure (or almost pure iron). Pure iron is relatively soft and less strong. Its melting point is about 1540°C. In industry, wrought iron is the material which is nearest to iron in purity; but is rarely used these days. Steel, on the other hand, is an alloy of iron and carbon; the percentage of carbon theoretically varies from 0 to 2%. However in actual practice, carbon rarely exceeds 1.25–1.3%. Carbon forms an inter-metallic compound called cementite (Fe3C), which is very hard, brittle and strong. The presence of cementite in steel makes steel much stronger and harder than pure iron. CLASSIFICATION OF STEELS Steel can be classified into (i) plain carbon steel, and (ii) alloy steel. Plain carbon steel is that steel in which the only alloying element present is carbon. In alloy steel, apart from carbon, other alloying 11  12 Manufacturing Processes elements like chromium, nickel, tungsten, molybdenum, and vanadium are also present and they make an appreciable difference in the properties of steel. Before we go further, readers must note that in steels, besides iron and carbon, four other elements are always present. These are S, P, Mn and Si. Removing these elements from steel is not a practical proposition. However, the effect of sulphur and phosphorus on the properties of steel is detrimental and their percentage is generally not allowed to exceed 0.05%. Similarly, the usual percentage of manganese and silicon in steel is kept below 0.8 and 0.3%, although their effect is not detrimental to the properties of steel. In fact, manganese counters the bad effect of sulphur. The presence of these four elements to the extent indicated does not put plain carbon steel into the category of alloy steel. However, if higher percentages of Mn and Si are intentionally added to steel in order to alter its properties, then the resulting steels come within the category of alloy steels. Plain Carbon Steels Since the properties of plain carbon steels are so dependent upon their carbon percentage, these steels are further classified into following categories on the basis of carbon percentage only: (i) Low carbon or dead mild steel having carbon below 0.15%, (ii) Mild steel having carbon between 0.15–0.3%, (iii) Medium carbon steel having carbon between 0.3–0.7%, and (iv) High carbon steels having carbon content above 0.7% (the higher practical limit of C% is 1.3%). As the carbon percentage increases, the strength and hardness of plain carbon steel increases while ductility decreases. Reference is invited to Fig. 2.1 (see figure on next page), which shows the effect of increasing carbon percentage on certain mechanical properties of carbon steels. Applications and Uses of Plain Carbon Steel Dead mild steel. It has got very good weldability and ductility. Hence, it is used in welded and solid drawn tubes, thin sheets and wire rods, etc. It is also used for those parts which undergo shock loading but must have good wear-resistance. To increase its wear-resistance, the parts have to undergo case hardening process; which provides a hard surface, while the core remains soft and tough. Mild steel. It is used very extensively for structural work. It retains very good weldability if carbon percentage is limited to 0.25%. Forgings, stampings, sheets and plates, bars, rods and tubes are made of mild steel. Medium carbon steel. It has little weldability but is stronger and has better wearing property than mild steel. It is used for railway axles, rotors and discs, wire ropes, steel spokes, marine shafts, carbon shafts, general agricultural tools etc. High carbon steels. It is used for hand tools like cold chisels, cold working dies, hammers, boiler maker’s tools, wood working tools, hand taps and reamers, filers, razors, shear blades etc. High carbon steels can be hardened by the process of quenching and being hard can be used for cutting tools which are not used in hot condition. If they become hot (above 150°C), they begin to lose their hardness and become blunt. Ferrous Materials 13 Dead Mild Mild Medium Carbon High Carbon Steel Steel Steel Steel Structural Sections, Tensile Strength Press Dies, Drills, Lathe Tools, Files Springs, Shears Milling Cutters, (N/mm ) Drop Forgings Springs, Tyres 2 Drop forgings Axles, Gears, % Elongation Rod, Sheet Hardness Brinell Taps 900 30 300 th ng t re S ile e ns T 600 ss rdne 20 200 ne l l Ha Bri Du 300 cti 10 100 lity (% Elo ng ati on ) 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.0 1.1 1.2 0.83 Carbon % Ferrite Cementite Ferrite Pearlite All Pearlite Pearlite Fig. 2.1 Microstructure, mechanical properties, and uses of plain carbon steels WROUGHT IRON It is the purest form of iron; although it may contain traces of carbon. It is usually made by ‘‘puddling process’’ and besides iron contains a small quantity of slag. It is very costly and its use has been almost totally replaced by cheaper steel. However, for some components like chain-links and chain-hooks wrought iron is still the preferred raw material. In old havelis/houses, one can still see iron railings and gates made of wrought iron.  14 Manufacturing Processes CAST IRON Cast irons contain more than 2% carbon, which is the theoretical limit for steels. However, in actual practice, carbon content of most cast irons is between 3 to 4 per cent. One characteristic of cast irons (except white cast iron) is that much of the carbon content is present in free form as graphite. It is this fact, which determines, largely, the properties of cast iron. Cast iron is generally produced in coke-fired cupola furnaces by melting a mixture of pig iron, scrap cast iron and a small percentage (usually not exceeding 5%) of small sized steel scrap. Melting point of cast iron is much lower than that of steel. Most of the castings produced in a cast iron foundry are of grey cast iron. These are cheap and widely used. There are many varieties of cast iron. These are listed below: (i) Grey cast iron, (ii) White cast iron, (iii) Malleable cast iron, (iv) Nodular cast iron, and (v) Alloy cast iron. As already mentioned, Grey cast iron is very widely used in the form of castings. In fact, it is so widely used that the term cast iron has come to mean grey cast iron. If a finger is rubbed on a freshly fractured surface of grey cast iron, the finger will get coated with grey colour due to the graphite present in the cast iron. Grey cast iron has good compressive strength, but is weak in tension. It is relatively soft but brittle. It is very easy to machine and the resulting surface finish is good. It is self lubricating due to presence of graphite and has good vibration damping characteristics. Compared to steel, it resists corro- sion. Due to these properties, it is used extensively for making machine beds, slides, gear-housings, steam engine cylinders, manhole covers, drain pipes etc. White cast iron and malleable cast iron. White cast iron has 2 to 2.5% carbon and most of it is in the form of cementite. If molten cast iron is cooled very quickly and its chemical composition lacks graphite-promoting elements like Si and Ni, then carbon remains in combined form as Fe3C. However, white cast iron does not have much use as such. It is very hard and shows white coloured fracture. Only crushing rolls are made of white cast iron. But it is used as raw material for production of malleable cast iron. Malleable cast iron is manufactured by a complex and prolonged heat treatment of white cast iron castings. Grey cast iron is brittle and has no or very little elongation. Malleable cast iron castings loose some of grey iron’s brittleness and become useful even for those applications where some ductility and toughness is required. (Note: ‘‘Mottled iron’’ is a name given to cast iron whose structure shows part grey and part white cast iron characteristics.) Nodular cast iron. This cast iron is also known under the name of spheroidal graphitic cast iron. If a little bit of magnesium (0.5%) is added to molten cast iron, the graphite, which is normally present in grey iron in the form of graphite flakes, changes its shape to small balls/spheres and remains distri- buted throughout the mass of cast iron. This change in the shape of graphite particles has a very big Ferrous Materials 15 effect on the properties of resulting castings and their mechanical properties improve considerably. The strength increases, yield point improves and brittleness is reduced. Such castings can even replace some steel-components. Alloy cast iron. The properties of cast iron can be improved by addition of certain alloying elements like nickel, chromium, molybdenum and vanadium, etc. Alloy cast irons have higher strength, heat-resistance and greater wear-resistance etc. Such enhanced properties increase the application and uses of cast irons. I.C. engine cylinders, cylinder liners, piston rings etc. are made of alloy cast irons. ALLOY STEELS Just as the properties of cast iron can be improved by adding some alloying elements to its composition, so can the properties of plain carbon steels be improved tremendously by addition of alloying elements. In fact, in the case of steels, the effect of alloying is much more marked. The main object of alloying in steels are: (i) Alloy steels can be hardened by heat treatment processes to greater depth and with less distortion and less chance of cracking. (ii) Alloying develops corrosion resisting property as in stainless steels. (iii) Alloying develops the property of red hardness as in cutting tool. (iv) Alloying develops the strength and toughness of steels as in high strength low alloy (HSLA) steels. (v) Some alloy steel show a marked resistance to grain growth and oxidation at high temperatures etc. Main alloying elements used are chromium, nickel, tungsten, molybdenum, vanadium, cobalt, manganese and silicon. Alloy steels are available in a great variety, each one has been developed for a specific purpose. We shall study them by grouping them in (i) stainless steels, (ii) tool steel and (iii) special steels. Stainless steels. These steels are called stainless because they do not corrode or rust easily. Main alloying elements used are chromium and nickel. Stainless steels are further divided into the following three categories: (i) Ferritic stainless steel. These steels contain a maximum of 0.15% carbon, 6–12% chro- mium, 0.5% nickel besides iron and usual amounts of manganese and silicon. These steels are stainless and relatively cheap. They are also magnetic. These days, one and two rupee coins are made from such steels. These steel are essentially Iron-chromium alloys and cannot be hardened by heat treatment. Main usage for such steel is in manufacture of dairy equipment, food processing plants, chemical industry etc. (ii) Martensitic stainless steel. These stainless steels have 12–18% chromium but contain higher carbon percentage (0.15–1.2%). These steels can be hardened by heat treatment, but their corrosion resistance is reduced. These steels are used for making surgical knives, hypodermic needles, bolt, nut, screws and blades etc. (iii) Austenitic stainless steels. These are the most important and costliest among all stainless steels. In these steels, besides chromium, nickel is also added. Nickel is a very strong austenite stabi- liser and therefore the microstructure of these steels is austenitic at room temperature. The most com-  16 Manufacturing Processes mon amongst stainless steel is 18/8 steel. Its composition is 18% chromium, 8% nickel, 0.08–0.2% carbon, manganese 1.25% maximum and silicon 0.75% maximum. Such steels have extremely good corrosion resistance but they cannot be hardened by heat- treatment. However, they are very susceptible to ‘‘strain-hardening’’. In fact, due to strain hardening, their machining becomes very difficult. It is used extensively for household utensils and in chemical plants and other places where high corrosion resistance is required. Tool steels. The requirements in a tool steel are that it should be capable of becoming very hard and further, that it should be able to retain its hardness at high temperatures commonly developed during cutting of steel and other materials. This property is called ‘‘red hardness’’. Further tool steel should not be brittle and should have good strength. High speed steel (HSS) is the name given to a most common tool steel. Its name implies that it can cut steel at high cutting speeds. At high cutting speed, the temperature rise is higher but high speed steel tools can retain their hardness up to 600–625°C. The property of red hardness comes from addition of tungsten. A typical composition of H.S.S. is tungsten 18%, chromium 4%, vanadium 1%, carbon 0.75–1%, rest iron. Tungsten is a costly metal. It has been found that molybdenum can also impart ‘‘red hardness’’ to steel and actually half per cent of molybdenum can replace one per cent of tungsten. Molybdenum is far cheaper than tungsten. H.S.S. with tungsten are known as T-series and H.S.S. with molybdenum are known as M-series steels. A very useful H.S.S. has a composition of tungsten 6%, molybdenum 6%, chromium 4% and vanadium 2%, besides iron and carbon. Another version of H.S.S. is called super high speed steel. It is meant for heavy duty tools and has about 10–12% cobalt, 20–22% tungsten, 4% chromium, 2% vanadium, 0.8% carbon, rest iron. These days, tools are made of tungsten carbide and other materials, besides H.S.S. Special Alloy Steels (i) Manganese steels. All steels contain small amounts of manganese to mitigate the bad effects of sulphur. The true manganese alloy steels contain much larger amounts of Mn. They have work hardening properties. They are used for railway points and crossings, and with usage, they become more wear-resistant. (ii) Nickel steels. Nickel can be added in steels up to 50%. Nickel makes the steel highly resistant to corrosion, non-magnetic, and having very low coefficients of thermal expansion. Such steels are used for turbine blades, internal combustion engine valves etc. (iii) Chromium steels. Chromium makes steel corrosion resistant, and increases its UTS. and IZOD strength. Very often alloy steels are used with both chromium and nickel being added. Ni-Cr steel wires are often used in furnaces, toasters and heaters. (iv) Silicon steels. A steel containing 0.05% carbon, about 0.3% Mn and 3.4% of silicon possesses extremely low magnetic hysteresis and is used widely for making laminations of electrical machines. Silico-manganese steels are also used frequently for making springs. Ferrous Materials 17 HEAT TREATMENT OF CARBON STEELS Object of heat treatment. Metals and alloys are heat treated to improve their mechanical properties, to relieve internal stresses or to improve their machinability. The properties of carbon steels can also be altered significantly by subjecting them to heat treatment processes. Heat treatment consists of three basic steps: (i) Heat the metal/alloy to a predetermined temperature. This temperature will, ideally, depend upon the actual composition of carbon steel (i.e. carbon percentage), (ii) Soaking or holding the metal/alloy at that temperature for some time, so that the temperature across the entire cross-section becomes uniform, and (iii) Cooling the metal/alloy at a predetermined rate in a suitable medium like water, oil or air. The rate of cooling is the most important factor. Kinds of Heat Treatments Given to Carbon Steels Carbon steels are subjected to the following four basic heat-treatment processes: (i) Annealing, (ii) Normalising, (iii) Hardening, and (iv) Tempering. We shall now describe these processes very briefly. Annealing. The purpose of annealing is to soften the material. Along with softening, the internal stresses, if any, will also get removed. The approximate temperatures to which the steel-sample should be heated will depend upon its carbon content. The recommended temperatures are shown in the following table: Table 2.1 Material Annealing temp. (°C) Dead mild steel (Carbon < 0.15%) 870–930 Mild steel (Carbon 0.15–0.3%) 840–870 Medium carbon steel (Carbon 0.3–0.7%) 780–840 High carbon steel (Carbon 0.7–1.5%) 760–780 Soaking time may be given at the rate of 3-4 minutes for everyone mm thickness of the cross- section of material. In annealing, the work piece is allowed to cool inside the furnace only after switching off electrical power or oil supply to the furnace. This ensures that the work piece cools at a very slow rate. This process results in softening of material and increase in ductility due to grain growth. Normalising. Normalising entails heating to the same temperatures as recommended for annealing (except for high carbon steel specimens, which are to be heated to much higher temperatures than for annealing particularly as carbon percentage in sample increases), soaking and then cooling the sample in still air. Main object of normalising is getting rid of internal stresses and grain-refinement.  18 Manufacturing Processes Hardening. Hardening involves heating (to the same temperatures as in case of annealing) and soaking. Thereafter, the work piece is taken out of the furnace and quickly cooled at a very fast rate in a tank of cold water or oil, agitating the water/oil vigorously. (This cooling operation is called ‘‘quenching.’’) The result is hardening of the work piece. However, in order to harden, the carbon content in the work piece should be at least 0.25%. Therefore, dead mild steel cannot be hardened in this way. Mild steel will also harden slightly for specimens containing over 0.25% carbon. Higher the carbon percentage, higher will be resulting hardness. Hardened pieces become brittle and their extreme brittleness becomes a great disadvantage. They tend to fail in-service. Therefore hardening process is invariably followed by a tempering proc- ess. Tempering. Tempering means giving up a certain amount of hardness but shedding a great deal of brittleness acquired in the process of hardening. It is a trade off between hardness and brittleness, so that hardened component may give useful service without failure. Tempering involves heating the carbon steel part to a temperature varying from 150°–600°C (depending upon how much trade off is required) and cooling the component in an oil or salt bath or even in air. Case hardening. As mentioned above, only those carbon steels can be hardened whose carbon content is about 0.25% or more. How do we harden dead mild steel? The answer is by case hardening. In this process, the work piece is packed in charcoal and heated as in annealing. It is kept at that high temperature for a few hours. The result is that carbon enters into the surface of the work piece to the depth of a mm or two depending upon the heating time. The work piece now has a case where carbon percentage is as per requirement for hardening. It is then heated and quenched in the usual manner. The result is a component whose surface acquires hardness, but core remains soft and tough. QUESTIONS 1. What is the importance of ferrous materials in our daily lives? 2. What is steel? How is it different from iron? Differentiate between plain carbon steels and alloy steels. 3. What are the characteristic properties of cast iron? 4. Describe the object of annealing. How is it different from ‘‘normalising’’? 5. Describe the process of hardening steel. Why are hardened objects subjected to tempering treat- ment after hardening them? 6. Write a brief note about stainless steels. What constituent of such steels render them corrosion- resistant. 7. What are different types of cast irons? 8. What is the object of alloying steels?  +0)26-4 ! Non-Ferrous Metals and Alloys INTRODUCTION Non-ferrous metals and alloys do not contain any significant quantity of iron. The most common non- ferrous metals used in engineering applications are copper, aluminium, tin, lead and zinc. Nickel, magnesium and antimony are also used for alloying the aforesaid non-ferrous metals. PROPERTIES AND USES OF NON-FERROUS METALS Copper. Copper is a corrosion resistant metal of an attractive reddish brown colour. It is an extremely good conductor of heat and electricity. It can also be drawn in wires, beaten into sheets and plates. Hence, it is extensively used in electrical industry for making armature coils, field coils, current carrying wires, household utensils etc. But its great usefulness lies in the fact that it alloys with zinc, tin and nickel to yield brass, bronze and cupro-nickels respectively which are widely used in engineering industry. Copper, as such, is used for many decorative items. Not much of copper is available in India. We import at least 50–60% of our requirement every year. Aluminium. Aluminium metal is difficult to extract from its main ore called bauxite. However, bauxite is available in India very plentifully and we have a thriving aluminium industry. Aluminium is also very corrosion resistant (because an adherent oxide layer protects it from further oxidation). It is again a very good conductor of heat and electricity (although not as good as Cu). It is ductile and malleable and is much cheaper than copper. Hence, it has all but replaced copper wires for transmission of electricity. It is also used for household utensils including pressure cookers. However, since it can be converted into thin foils, it is now extensively used for beverage cans and in packaging industry. Its density is about a third of steel, hence it is also used for aircraft and helicopter frames and in transport vehicles. Sometime ago, in India, 1, 2, 5, 10 and 20 paisa coins were made of an aluminium-magnesium alloy. Aluminium forms a series of alloys with magnesium, which are harder and stronger than pure aluminium. Tin. It has an attractive silvery white colour. It has very good resistance to acid corrosion. Before the advent of plastic tin coated steel sheets of thin gauge were used for manufacture of 19  20 Manufacturing Processes tin-containers for storage of ghee, mustard and other oils. Today tin is mostly used for alloying pur- poses. Tin and lead melted together give a series of soft-solders. Tin has a low melting point. Lead. Lead is a heavy metal with dull grey appearance. It has good corrosion resistance and has got good malleability. In Europe, it was extensively used for roof protection. It was also used in plumb- ing. It can withstand sulphuric acid and previously this acid used to be stored in lead lined vessels. It has self lubricating properties. It was therefore used in lead-pencils. Sometimes, a small quantity of lead is added to steel and tin bronze to impart free cutting properties. Zinc. Zinc possesses a bluish grey metallic appearance. It has high corrosion resistance. In fact, steel sheets are often covered by a thin coating of zinc. Such zinc coated sheet are known as galvanised iron sheets (G.I. sheets). The zinc coating provides protection to steel sheets from corrosion for many years. Zinc has a low melting point and high fluidity making it suitable for items to be produced by die- casting process. Zinc is incidentally much cheaper than either copper or tin; making brass, an alloy of copper and zinc much cheaper than copper or tin-bronze. Zinc is also used in torch light batteries. In the following table, colour, tensile strength, melting point–specific gravity and important properties of some non-ferrous metals are given. Table 3.1 Metal Tensile Colour Specific M.P. strength Gravity (°C) Few important properties N/mm2 Copper 160 Reddish brown 8.9 1083 Good conductor, soft, ductile and malleable Aluminium 60 White 2.7 660 Good conductor, very soft, ductile and malleable Tin 13 Silvery white 7.3 232 Good appearance, acid resistance, soft Lead 15 Dull grey 11.4 327 Very heavy, good corrosion resistance against H2SO4 Zinc 155 Bluish, white 7.1 419 Good corrosion resistance and fluidity when molten Note: For comparison, tensile strength of Iron is 270 N/mm2. ALLOYS OF COPPER Brass Brass is an alloy of copper and zinc. Commercially, two types of brasses are most important: 1. Alpha brass. It contains up to 36% zinc and remainder is copper. 2. Alpha-Beta brass. It contains from 36% to 46% Zn, remainder is copper. Alpha and Beta are names given to different phases of brasses. Alpha-Beta brass contain both alpha and beta phases. The tensile strength and ductility of brass both increase with increasing Zn content up to 30% zinc. If zinc content increases beyond 30%, the tensile strength continues to increase up to 45% Zn, but Non-Ferrous Metals and Alloys 21 there is a marked drop in ductility of brasses. β-phase is much harder and stronger but less ductile than α-phase. α-phase has excellent cold-formability and is used where the parts are wrought to shape. The mechanical properties of α-brasses also change with the amount of cold-work done on them. α-β brasses are fit for hot working. α-brasses can be sub-divided into two groups— (i) red-brasses containing up to 20% Zn, and (ii) yellow brasses containing over 20% Zn. Red brasses are more expensive and are primarily used where their colour, greater corrosion resistance or workability are distinct advantages. They have good casting and machining properties and are also weldable. One well-known red-brass is ‘‘gilding-brass’’ or gilding metal with 5% Zn. It is used for decorative work.Yellow brasses are most ductile and are used for jobs requiring most severe cold forging operations. The cartridges are made from a 70% Cu, 30% Zn brass by a deep drawing process, hence this composition of yellow brass has come to be known as cartridge brass. Other famous compositions of brasses are: Admirability brass containing 29% Zn, 1% Tin, remaining copper. Muntz’ metal contains 40–45% Zn, remainder is copper. Naval Brass contains 39% Zn, 1% Tin, remainder is copper. Admiralty brass, naval brass and muntz metal are all used for ships-fittings, condenser tubes, preheaters, heat exchangers etc. Bronzes Bronze is an alloy of copper and tin although commercial bronzes may contain other elements besides tin. In fact, alloys of copper with aluminium, silicon and beryllium, which may contain no tin are also known as bronzes. Tin bronzes are of a beautiful golden colour. As in brasses, both tensile strength and ductility of bronzes increase with increases in tin content. However, more that 10% tin is not used in bronze as it results in the formation of a brittle intermetallic compound, Cu3Sn. Addition of tin to copper up to 10% increases the strength, hardness and durability to a much greater extent than the addition of zinc to copper. The following varieties of tin bronzes are commonly used: (i) Phosphor-Bronze. Addition of 0.5% phosphorous to tin bronze results in production of phosphorous bronze. Phosphorous increases fluidity of molten metal and fine castings can be made. (ii) Leaded-Bronze. Addition of lead to tin bronze, results in production of leaded bronze. Lead is actually a source of weakness, but adds to machinability and has self lubricating properties. Usually, lead percentage does not exceed 2%. (iii) Gun-metal. It contains 2% zinc, 10% tin and 88% copper. It is a very famous composition. This bronze is used for bearing bushes, glands, pumps, valves etc. (iv) Bell-metal. It is a tin bronze but having a very high percentage of tin (20–25%). It gives a good tinkling sound on being struck with a hammer.  22 Manufacturing Processes Bronzes having no tin. The following bronzes contain no tin and are commercially well-known: (i) Aluminium bronze. Composition: 14% Aluminium, rest copper. It possesses good strength and good corrosion resistance. Colour: golden yellow. Often used for costume jewellery. (ii) Silicon bronze. Composition: 1–4% Silicon, rest mainly copper. Possesses extremely good corrosion resistance. Can be cold worked and strain-hardened. Used for boiler fitting and marine fittings. (iii) Manganese bronze. Composition: 40% zinc and 55–60% copper with 3–5% manganese. It is essentially a brass to which manganese has been added. It is used for ship’s propellers. (iv) Beryllium bronze. Beryllium is very costly. So is this alloy. It contains about 2% Be. It has very good mechanical properties and can be cold worked and age-hardened. It is mainly used for bellows, bourdon gauge tubes etc. CUPRO-NICKELS Cupro-nickels are alloys of copper and nickel. Copper and nickel, when melted together in any propor- tion are perfectly miscible and dissolve each other. When the alloy solidifies, the solubility continues forming a solid solution. Cupro-nickels are silvery white in colour and have extremely good corrosion-resistance. They are extensively used for marine fittings. They also possess good strength, hardness and ductility. Coins of rupee five are made of 75% copper and 25% nickel. However, another alloy containing 45% Ni and 55% copper is called ‘‘constantan’’. It is used for manufacture of thermocouples, low temperature heaters and resistors. ALUMINIUM ALLOYS Aluminium as such is a soft metal of relatively low strength. Most of the alloys of aluminium are made by alloying it with various percentages of magnesium; these are harder and stronger. These alloys known as L-M series alloys can be extruded and are used extensively for structural work. A famous alloy of Aluminium containing 4% copper, 0.5% magnesium, 0.5% manganese, a trace of iron and rest aluminium is called DURALUMIN. It has high strength and a low specific gravity. However, its corrosion resistance is much lower as compared to pure aluminium. Sometimes, duralumin is covered or clad by thin aluminium layer on all sides. Such material is called ALCLAD and is used in aircraft industry. If 5–15% silicon is alloyed with aluminium, we get alloys which are temperature resistant. Cast- ings made of Al-Si alloys are used for manufacture of pistons of two wheelers on a large scale. ALLOYS OF NICKEL (i) German silver. It is a cupro nickel to which zinc has been added. A typical composition is 60% copper, 30% nickel and 10% zinc. Addition of zinc brings down the cost. Its colour is silvery with a slight pale tinge. It is very ductile and malleable and corrosion resistant. It is used for making electrical contacts, costume jewellery and high quality taps etc. Before the advent of stainless steel, it was also used for household utensils and coinage. Non-Ferrous Metals and Alloys 23 (ii) Monel metal. Its composition is 68% nickel, 30% copper, 1% iron, remainder manganese etc. (iii) Nichrome. Alloy of nickel and chromium, which is used as heat resistant electrical wire in furnaces, and electrical heating devices like geysers, electric iron etc. (iv) Inconel and incoloy. Alloys principally containing, nickel, chromium and iron. Used in electrical industry. QUESTIONS 1. Differentiate between ferrous and non-ferrous materials. 2. What are characteristic properties of copper and aluminium, which make them useful to man- kind? 3. Differentiate between bronzes and brasses. Mention two applications of each. 4. Write a short note on aluminium and its alloys. 5. What are the different types of brasses you know? Distinguish between Naval and Admiralty brass. 6. What are cupro nickel? What are their main properties and applications?  Objective Type Questions Pick out the most appropriate option: 1. Mild steel is an alloy of iron and carbon with percentage of carbon ranging from (a) up to 0.2% (b) 0.15–0.3 (c) 0.3–0.5 (d ) above 0.5. 2. IZOD test measures (a) hardness (b) ductility (c) impact-strength (d ) grain size. 3. Copper is used for making electrical conductors because it is (a) ductile (b) resists corrosion (c) has low resistance (d ) cheap. 4. Brass is an a